采用反相悬浮聚合法合成了聚丙烯酸高吸水性树脂。
A high water absorption polyacrylic acid resin was obtained using inverse suspension polymerization.
采用反相悬浮聚合法合成聚丙烯酸钠高吸水性树脂。
Inverse suspension polymerization was adopted to synthesize sodium polyacrylate super hydroscopicity resin.
方法：利用悬浮聚合法制备PMMA/MMT复合物；
Methods:The PMMA/MMT nanocompounds were synthesized by suspension polymerization.
本文以丙烯酸为原料，采用反相悬浮聚合法合成高吸水树脂。
In this paper, a super absorbent resin that used acrylic acid as raw material and was synthetized by means of inverse-phase suspension polymerization was studied.
同时比较共混法与悬浮聚合法制得的复合材料在甲苯中的溶解性。
The dissolution of composites by mixing in toluene is compared with that by suspension polymerization.
用改进的悬浮聚合法制备了表面含有羧基功能团的聚苯乙烯磁性微球。
Carboxylate modified magnetic microspheres were prepared by using modified suspension polymerization method.
用改进的悬浮聚合法制备了表面含有羧基功能团的聚苯乙烯磁性微球。
Carboxylate modified magnetic microspheres were prepared by using modified suspension polymerization method. Their structure, size distribution and magnetic content were measured.
以4 -叔丁基苯乙烯为单体，采用自由基悬浮聚合法合成了颗粒状高吸油树脂。
Granular high oil-absorbing resin was prepared by free radical suspension polymerization process using 4-tert-butyl styrene as monomer.
本文采用悬浮聚合法制备三种高吸油性树脂，并考察了高吸油性树脂吸油性能的影响因素。
Three high oil-absorption resins were synthesized by suspension polymerization and the factors affected the properties of oil-absorption resins were investigated.
采用悬浮聚合法合成甲基丙烯酸酯类高吸油树脂，研究了交联剂、引发剂用量对树脂性能的影响。
A high oil-absorption resin of polyacrylic acid system with moderate crosslinking was synthesized by suspension polymerization.
采用悬浮聚合法合成甲基丙烯酸酯类高吸油树脂，研究了交联剂、引发剂用量对树脂性能的影响。
The oil-absorption of high oil-absorption resin, as an emerging technique to remove oil in environment, is causing widespread concern.
以丙烯酸酯为单体，二乙烯基苯为交联剂，采用悬浮聚合法合成低交联度的聚丙烯酸酯类吸油树脂。
The acrylate oil absorbing resin were synthesised by means of suspension polymerization and using divinylbenzene as crosslinking agent.
介绍一种采用悬浮聚合法制备彩色静电复印粉的新工艺，染料和其它添加剂是在聚合反应之前加入。
A new technology of preparing color electrophotographic toners by a suspension polymerization process in which the dyes and additives were mixed with the monomer prior to polymerization is presented.
以丙烯酸 2 -乙基己酯与醋酸乙烯酯为单体 ，采用悬浮聚合法 ，以单体自交联制得高吸油性树脂。
The high oil-absorption resin of copolymer of vinyl acetate and (2-ethylhexyl) acrylate was prepared by suspension polymerization with self-crosslinking.
采用悬浮聚合法合成了木浆纤维素交联聚合复合高吸油性材料，测定了所制备的复合高吸油性材料吸油性能指标。
The high oil-absorbing resin made of crosslinked copolymer of wood fibre and cetyl methacrylate was prepared by suspension polymerization method.
以丙烯酸酯为单体，二乙烯基苯为交联剂，三氯甲烷为致孔剂，采用悬浮聚合法合成了轻度交联的多孔丙烯酸酯类吸油树脂。
Using acrylate as monomer, divinyl benzene as crosslinking agent, chloroform as microvoid agent, acrylate resin was synthesized by means of suspension polymerization. It had low crosslinking density.
采用水相悬浮沉淀聚合法，以氧化还原体系为引发剂，合成了丙烯腈（AN）与丙烯酸甲酯（MA）的共聚物。
Using redox system as initiator, copolymerization of acrylonitrile(AN) and methacrylate(MA) was carried out via the method of aqueous suspension precipitation polymerization.
采用水相悬浮沉淀聚合法，以氧化还原体系为引发剂，合成了丙烯腈（AN）与丙烯酸甲酯（MA）的共聚物。
Using redox system as initiator, copolymerization of acrylonitrile(AN) and methacrylate(MA) was carried out via the method of aqueous suspension precipitation polymerization.