材料经固溶处理后析出物绝大多数都溶入基体。
Most precipitate dissolve into the matrix after solution treatment.
固溶处理温度对抗拉强度和延伸率有较大的影响。
Solution treatment temperature has a significant impact on the tensile strength and elongation.
对比测定了经固溶处理和未经固溶处理锯条的锯切性能。
The cutting performances of saw blade by solution and non-solution heat treating were determined.
经固溶处理和自然时效的铝铜合金可以进行硬质阳极氧化。
Hard anodizing film could be obtained on Al-Cu alloy surface which had been treated with solid solution treatment and natural aging.
在固溶处理时快速冷却过程中锰在奥氏体晶界产生不平衡偏聚。
During the fast cooling process of solution treatment, nonequilibrium segregation of manganese...
通过固溶处理后自然时效，能有效地提高合金的综合力学性能。
The results showed that natural ageing after solution heat treatment led to increase the comprehensive mechanical properties effectively.
复合材料固溶处理后硬度值较高是由合金元素的固溶强化所致。
The highest hardness of the composite in the solution state is due to the solution strengthening.
结果表明，固溶处理状态下母材氩弧焊时具有较低的冷裂纹敏感性。
The experimental results show that, under solution treatment condition, this alloy has lower cold-crack susceptibility.
研究了不同固溶处理对双相铸造不锈钢的组织及其耐蚀性能的影响。
The influence of different solid solution treatment on the structure and corrosion resistant property of cast duplex stainless steel was investigated.
研究了不同固溶处理对GH128高温合金晶粒度和显微组织的影响。
The effects of different solution treatments on the microstructure and grain size of GH128 Superalloy were studied.
固溶处理是改善和提高奥氏体不锈钢波纹管抗应力腐蚀能力的有效措施。
And solution treatment is the valid method to improve the anticorrosion property of the austenite stainless steel bellows.
分析了采用焊后固溶处理对SAF2205双相不锈钢耐腐蚀性能的影响。
The influence to corrosion resistant ability of duplex stainless steel (SAF2205) after solution treatment to weld joint.
该合金在固溶处理后塑性良好，易于辗压及加工成型各种形状复杂的零件；
The alloys in plastic after solution treatment good, easy Rolling and Processing of the various parts of complex shape;
本文研究高温固溶处理对一种定向凝固高强度镍基高温合金的组织和性能的影响。
The effect of high temperature solution treatment on the structure and properties of a directionally solidified high strength nickel-base superalloy has been investigated.
通过低压铸造后固溶处理的方法，获得了网状金属间化合物增强铝合金表面复合层。
Intermetallic compound foam reinforced aluminium alloy surface composite layer are obtained by solution treatment after low pressure Casting.
研究了镁基准晶中间合金和固溶处理工艺对AZ91合金显微组织和力学性能的影响。
Effects of master alloy of quasicrystal containing magnesium additions and solution treatment on microstructure and mechanical properties of AZ91 magnesium alloy were studied.
本文探讨了GH90合金弹簧钢丝的固溶处理、表面处理以及拉拔变形量和拉拔工艺。
This paper discusses the solid solution, surface treatment and drawing deformation and drawing process of GH90 alloy spring steel wires.
经过固溶处理后，焊缝组织晶粒变大，焊缝区和母材区弥散分布着大量的颗粒状析出物。
After solution treatment, the weld grains become coarse along with a large amount of granular precipitates dispersed in weld zone and base metal zones.
对原始组织为铸态和热轧态的2205双相不锈钢试样进行了不同条件下的固溶处理热模拟试验。
The solution treatments were performed with the specimens of 2205 duplex stainless steel, which possessed different initial microstructures.
研究了锰的质量分数、固溶处理温度和淬火冷却速度对锰不平衡偏聚的影响和不形成锰偏聚的条件。
It includes the effect of manganese content, solution treatment temperature and cooling rate on the non equilibrium segregation of manganese and condition of segregation formation.
固溶处理温度的高低不仅影响第二相在基体中的溶解程度，还影响合金的回复再结晶过程进行的程度。
The temperature of solid solution treatment affected not only the degree of the second phase dissolved in the matrix alloy, but also the recovery and recrystallization processing level of the alloy.
固溶强化效应的增加、位错密度的提高及硬质相邻接度的减少被认为是固溶处理改善韧性的主要原因。
The reasons are mainly due to the increase of solution strengthening and dislocation density in the binding phases, and the decrease of bonding degree among of hard phases.
介绍了固溶处理温度、淬火到时效间隔时间及时效制度等对2A70铝合金预拉伸厚板组织和性能的影响；
The effect of quenching temperature, the interval time from quenching to aging and aging institution to 2A70 aluminium alloy pre-stretching plate structure and properties are introduced.
装置具有温度采集、加热时间准确、及时冷却等优点，为不锈钢u形管固溶处理提供了自动化水平比较高的设备。
The device has these features that temperature acquisition, accurate heating time, timely cooling etc; it provides the high level automation device to steel U-tube solution treatment.
不锈钢薄壁焊管退火(固溶处理)是保证产品质量的关键工序，在实际生产中如操作和调整不当都会出现质量问题。
Annealing process is the key process to ensure the quality of stainless thick wall pipe. The improper operation and adjusting will induce the quality problem.
结果表明：经固溶处理的焊缝和热影响区，晶内奥氏体析出变少，晶粒尺寸变小，同时奥氏体的形状由长条状变为圆状。
The results show that the precipitated austenite crystals of welded joint after solid solution treatment are fewer, the grains are smaller. And the shape of austenite changes from strip to roundness.
结果表明：经固溶处理的焊缝和热影响区，晶内奥氏体析出变少，晶粒尺寸变小，同时奥氏体的形状由长条状变为圆状。
The results show that the precipitated austenite crystals of welded joint after solid solution treatment are fewer, the grains are smaller. And the shape of austenite changes from strip to roundness.