在化学镀镍-磷合金液中加入硫酸铜制得镍-铜-磷三元合金。
Electroless nickel copper phosphorus ternary alloy deposits were prepared by addition of cupric sulfate in electroless nickel phosphorus alloy plating bath.
介绍了化学镀镍-磷合金镀层的耐蚀特性及其在石化工业上的应用。
The anti-corrosion characters of chemical nicklephospherous alloy planting and its application in petrochemical industry are introduced.
由于具有优良的性能，化学镀镍磷合金在工业上得到了广泛应用。
Electroless Ni-P alloy deposits have been widely adopted in industries for their excellent properties.
化学镀镍磷镀层做为一门新型成熟的表面处理技术已受到人们越来越多的重视。
Chemical plating of nickel phosphorus film, as a new proven surface treatment technology, has drawn ever increasing attention.
以次亚磷酸钠为还原剂，在压电陶瓷表面进行酸性化学镀镍磷。
Acid electroless nickel phosphorus plating on PZT ceramic was studied with hypophosphite as a reducing agent.
结果表明，化学镀镍磷合金之后，镀态试样的疲劳寿命明显下降；
The results show that the fatigue life of electroless Ni-P alloy specimen could be dropped.
研究了酸性化学镀镍溶液中加速剂对沉积速度、氢的析出量、镀层含磷量和镀层耐腐蚀性能的影响。
Effect of the speeding additive on deposition rate, hydrogen evolution amount, content of phosphorus and corrosion resistance of deposit in acidic electrolyte has been studied.
本文对45钢彩色化学镀镍磷的镀液成分、工艺参数、着色方法进行了比较深入的研究。
Ingredients of the bath processing parameter and coloration method are studied deeply with respect to colored electroless Nickle plating on 45steel.
从镍磷化学镀的反应机理出发，讨论了反应中影响磷沉积速率和镀层中磷含量的主要因素，试验制备了含磷量较高且抗蚀性良好的镍磷镀层。
The chemical Ni P plating mechanism in acid baths and the major aspects which influence the plating rate and P content of Ni P alloy coatings were discussed.
这与普通化学镀镍磷明显不同。
This is obviously different from the common electroless nickel plating.
公司在化学镀镍磷领域拥有较高的知名度，产品远销海内外。
Companies in the field of electroless Ni-P has a higher profile, products sold at home and abroad.
通过正交试验法优选出一种具有高磷含量的快速化学镀镍工艺配方。
An electroless nickel plating process with high deposition rate was optimized by orthogonal test.
与传统化学镀镍工艺相比，该工艺所得镀层含磷量高、硬度高，组织结构致密均匀。
Compared with conventional electroless nickel plating process, the deposits obtained are greatly improved with higher phosphorus content, hardness, more compact and uniform microstructure.
本文采用电化学及量子化学手段，对化学镀镍磷过程中磷的析出机理及影响因素进行了深入的探讨。
Thus, electrochemical and quantum chemical methods were applied to deeply study phosphorus generation mechanism and influencing factors in this paper.
研究了在空心玻璃微珠表面化学镀镍磷合金的无钯活化新工艺。
By this activation process, electroless nickel on cenospheres surface was carried out.
化学镀镍磷合金具有很多独特的理化性能，然而由于成本较高限制了其应用。
Electroless nickel-phosphorus alloy deposit has many peculiar physical and chemical properties, yet its application is limited for high cost.
在化学镀镍磷合金工艺中，使用了一种新型的镀镍光亮剂en6 5d，获得了全光亮的镀层。
A new brightening agent EN65D is used in the electroless plating Nickel Phosioporuos process, and the entire bright coating is obtained.
采用化学镀技术在预处理后的金属表面上制备镍磷二元和镍铜磷三元镀片，用X射线光电子能谱分析仪和扫描电镜分别对镀片表面的元素价态、组成及镀片表面的形貌进行表征。
The coatings of nickel-phosphor and nickel-copper-phosphor are prepared on the pretreated metal surface by electroless plating technology. The coating surface has been characterized by XPS and SEM.
由于具有优良的性能，化学镀镍磷合金在工业上得到了广泛应用。
Preparation of bulk amorphous Ni-P alloy by electrochemical deposition and its structure research;
由于具有优良的性能，化学镀镍磷合金在工业上得到了广泛应用。
Preparation of bulk amorphous Ni-P alloy by electrochemical deposition and its structure research;