同时通过高低周复合试验,证明了高频载荷对疲劳寿命的影响。
Experimental results emphasize the influence of high-cycle loads to the fatigue life.
结果表明:与纯低周载荷作用相比,高低周复合载荷下球墨铸铁的裂纹扩展速率明显加快,极大地降低材料的疲劳寿命。
The results show that the crack growth rate under high-low cycle complex fatigue load is greater than that under low cycle fatigue load, and so the fatigue life is obviously reduced.
采用光滑圆棒和中心孔板片试样,对GH901合金室温高低周复合疲劳进行了系统的研究。
The fatigue behaviours of Superalloy GH901 under major combined with minor cycle have been systematically studied at room temperature using smooth specimen and sheet with center hole.