锌铁合金是锌与铁以金属键结合的混合物,是一个整体,表现出均一的物理和化学性质.
The phase structure of Zn-Fe alloy coating was Fe_4Zn_9,and it didn't change by using pulse plating or passivating. The SEM results showed that the coating was smoother and more even by pulse plating.
锌铁合金镀层中合金相结构为Fe_4Zn_9,采用脉冲电镀不能改变合金相结构,钝化以后合金相结构也未发生变化;脉冲电镀比直流电镀所获的合金镀层平滑均匀。
参考来源 - 脉冲电镀ZnBlack chromate passivation films on zinc and zinc-iron alloy coating have been used to improve the corrosion resistance, and the decorative properties of the substrates.
六价铬黑色钝化工艺通常用于提高锌及锌铁合金镀层的耐蚀性能和装饰性能。
参考来源 - 锌及锌铁合金镀层三价铬黑色钝化工艺研究·2,447,543篇论文数据,部分数据来源于NoteExpress
简要介绍了已开发的多层镍电镀工艺、铜锡合金、铜锌合金、锌铁合金、镍铁合金等代镍工艺,以及厚(薄)铜薄镍电镀工艺。
The developed processes such as multi-layer nickel plating, tin-copper alloy plating, zinc-copper alloy plating, iron-zinc alloy plating, iron-nickel plating and thick copper with thin nickel la...
为了保持基体金属硬度、磁性以及电镀层性能等均不变,将锌铁合金电镀工艺与磷化工艺进行了组合,以提高钢铁件的防护性能。
Holding primary hardness, magnetism and plating properties of matrix, protection performance of steel was improved by combining the Zn - Fe alloy electroplating and phosphating technology.
通过采用小压缩率多道次拉拔工艺,减少锌-铁合金的厚度,积极采用人工时效工艺等解决了拉拔困难的问题。
The drawing difficulty is settled by adopting small draught and multi-pass drawing process, reducing the thickness of Zn-Fe alloy and using artificial aging process actively.