A method calculated emissivity of billet surface is introduced in the paper.
本文介绍了一种计算铸坯表面发射率的方法。
参考来源 - 铸坯表面发射率的计算方法研究·2,447,543篇论文数据,部分数据来源于NoteExpress
连铸过程连铸坯表面裂纹是影响连铸坯质量的重要问题。
Surface cracks on slab are one of the important quality problems during continuous casting.
三角口裂纹、直线裂纹和渣孔是连铸坯表面夹渣的主要表现形式。
Triangle crack, linearity crack and slag eye are main form of surface wrapped slag in continuously cast billet.
据此认为,连铸弯月面温度波动是导致铸坯表面缺陷产生的一个重要原因。
It is considered that the temperature fluctuation of meniscus is a key factor for the surface defect formation of continuous casting billets.