熔融温度升高时,聚醚醚酮的结晶峰强度减弱,峰宽增加;而冷结晶峰温度提高。
With increasing melting temperature, the cold crystallization peak temperature increases, the crystallization peak strength of PEEK weakens and the peak width increases.
熔融时间延长时,聚醚醚酮的玻璃化转变温度和冷结晶峰温度均提高,熔融峰强度减弱。
On the other hand, both the glass temperature and cold crystallization peak temperature of PEEK increases and melting peak strength decreases while the melting time becomes longer.
报道了一种可溶性可控交联聚芳醚酮(CCPAEK)热塑性复合材料的制备方法。
The forming process of a thermoplastic Controllable Crosslinking Poly(Aryl Ether Ketone)(CCPAEK) matrix composite was reported in this paper.