... texture咬花 thermal refining调质处理 thermoechanical treatment加工热处理 ...
基于842个网页-相关网页
... 调整器regulator 调质处理quenching with Subsequent tempering 调质砂tempering sand ...
基于134个网页-相关网页
... hardening agent 固化剂；[化]硬化剂；淬火剂 hardening and tempering 调质处理 hardening effect 硬化效应 ...
基于100个网页-相关网页
Hardness of armor steel is boosted after it austenized at temperature 20℃higher than Ac3 in the second quenched and tempered process,4.
3、二次调质处理则在仅高于Ac3二十度左右进行奥氏体化保温,该工艺可以有效提高装甲钢的硬度。
参考来源 - GY4装甲钢组织相变规律及力学性能提高研究If sludge had a mechanical dehydration after modified treatment, it can only be separated free water and water space.
污泥经过调质处理后进行机械脱水,只能分离自由水和间隙水。
参考来源 - 酒精糟液污泥处理与有机复混缓释肥料研究·2,447,543篇论文数据，部分数据来源于NoteExpress
要达到所需的力学性能，一般要对其进行调质处理。
To meet such a need, it is generally required to get such pipes quenched and tempered.
这样，适当选择水温，45钢制较大截面工件的热水处理可代调质处理。
Therefore, selecting the water temperature properly the hot water processing of big cross section machine parts of 45 steel can replace modified treatment.
调质处理采用真空处理，可以减小热处理变形，可以提高工件表面质量。
The vacuum treating not only reduces the distortion but improves the parts' surface quality.
调质处理就是指淬火加高温回火的双重热处理方法，其目的是使工件具有良好的综合机械性能。高温回火是指在500-650℃之间进行回火。 调质可以使钢的性能，材质得到很大程度的调整，其强度、塑性和韧性都较好，具有良好的综合机械性能。调质处理后得到回火索氏体。回火索氏体(tempered sorbite)是马氏体于回火时形成的，在光学镜相显微镜下放大500~600倍以上才能分辨出来，其为铁素体基体内分布着碳化物（包括渗碳体）球粒的复合组织。它也是马氏体的一种回火组织，是铁素体与粒状碳化物的混合物。此时的铁素体已基本无碳的过饱和度，碳化物也为稳定型碳化物。常温下是一种平衡组织。