The results show that the best materiel ratio is graphite:potassium permanganate:mixed acid=1:0.11:3 at the room temperature. The expansion volume of product is 180mL/g at 300℃,400mL/g at 600℃.
研究制备低温可膨胀石墨的最佳条件:室温条件下,最佳物料比为:石墨:高锰酸钾:混酸=1:0.11:3(质量比),制得在300℃时膨胀容积为180mL/g;600℃时膨胀容积可为400mL/g的低温可膨胀石墨。
参考来源 - 低温可膨胀石墨的制备研究The expanded volume could reach to 760 ml/g. Exfoliated graphite was worm-like particles and made up of many graphite pieces, there were many pores inside it.
此条件下制备的膨胀石墨的膨胀容积高达760 mL/g。
参考来源 - 膨胀石墨改性复合物电极的制备及其降解有机物的研究·2,447,543篇论文数据,部分数据来源于NoteExpress
膨胀容积是影响膨胀石墨产品质量的重要因素。
Expanded volume was one of the important factors influencing expanded graphite product quantity.
通过混酸法制备了两种不同氧化剂体系的可膨胀石墨(EG),并采用膨胀容积和X射线(XRD)对EG进行了表征。
Two EG systems doped different oxidants were prepared by blended acid and characterized by expandable capacity and XRD.
膨胀石墨对重油的吸附量随着膨胀容积的增大而增加,合适的电流密度、电解液浓度以及反应时间是制备高膨胀容积膨胀石墨的关键。
Adsorption quantity increases with the expanded volume. Appropriate current density, electrolyte concentration and reaction time are the keys to obtain high-expanded volume.