聚合温度(polymerization temperature)指聚合反应正常进行时的温度。 自由基聚合一般在50~80℃下进行,阳离子聚合一般在0℃以下的温度进行,阴离子聚合一般在0℃以下或室温下进行。
The optimization condition is as follow: polymerization temperature: 43℃; ratio of St and DVB is 50:50 (w/w).
最佳聚合条件为:聚合温度:43℃;St:DVB=50:50(w/w)。
参考来源 - 炔丙磺酰胺螺旋聚合物的制备与应用研究The effects of reaction temperature,mass of surfactant,mass of initiator and mass of PSG on the polymerization conversion were investigated.
考察了聚合温度、乳化剂用量、引发剂用量和PSG用量对细乳液聚合转化率的影响。
参考来源 - 含氟接枝共聚物为助稳定剂的苯乙烯细乳液聚合反应Raising polymerization temperature and decreasing the amount of crosslinking monomer in the synthes ins of the thickener will improve the anti fiushing property of the products.
研究发现,提高聚合温度可以提高聚合产物的抗渗化性,但配制高粘度印花浆时对增稠效果不利,而在配制低粘度印花浆时则反之。
参考来源 - 影响涂料印花增稠剂增稠及抗渗化性能的因素·2,447,543篇论文数据,部分数据来源于NoteExpress
考察了聚合温度、体、联剂和溶剂萃取树脂对高吸油性树脂吸油性能的影响。
The effect of polymeric temperature, monomers, crosslinking agents and solvent -extraction on absorbency of high oil - absorbent resin were investigated.
考察了聚合温度、 单体、交联剂和溶剂萃取树脂对高吸油性树脂吸油性能的影响。
The effect of polymeric temperature, monomers, crosslinking agents and solvent-extraction on absorbency of high oil-absorbent resin were investigated.
结果表明,单体加入速度、聚合温度及引发剂用量是决定聚合物分子量的主要因素。
It has showed that the feeding speed of mixed monomers, temperature for polymerization and the dosage of initiator are main factors controlling the molecular weight.