经高温扩散退火处理后,显微硬度均匀性显著提高。
Uniformity of microhardness improved significantly after high temperature diffusion annealing.
结果表明:名义尺寸相同而实际尺寸相差较大的磨球所磨出的粉体粒度大且分布不均匀,烧结体硬质相颗粒粗大且等轴性差,抗弯强度和硬度均较低。
It is found that the grain size of the powders milled by balls with different diameters is big, the hard phase is big too and not uniform, the hardness and bending strength are also lower.
结果表明:回火索氏体是最佳的组织形态;微观硬度的不均匀性显著影响钢的表面加工质量。
The results indicated that the tempered sorbite was the optimum microstructure, the inhomogeneous distribution of micro hardness affected markedly the finish quality of the steel surface.