对呋喃树脂砂球墨铸铁件表层球化衰退原因进行了分析。
The reason causing nodularization degeneration in surface layer of furan resin sand nodular iron castings was analyzed.
大型厚断面球墨铸铁件在铸造过程中极易产生缩孔、缩松、石墨漂浮及球化衰退等铸造缺陷。
Large thick-section ductile Iron housing easily produces casting defects such as shrinkage cavity, shrinkage porosity, graphite floating and spheroidizing decay.
研究了镧镁球化剂的球化能力及其对球墨铸铁白口敏感性和抗衰退性的影响。
The nodulizing power of the La-Mg nodulizer and its influences on the chilling sensitivity of nodular cast iron and the property of anti-degeneration were studied.