研究了热浸渗铝钢扩散层空洞对循环氧化和剥落性能的影响规律及其机理。
The effects of the voids in the diffusion layer on cyclic oxidation and spalling resistance of aluminized steel was investigated.
用等离子喷涂方法在合金圆柱体上制备了热障涂层,并用水冷的方法进行了热冲击实验,试样的失效现象为轴向的开裂和剥落。
The plasma spraying technique was used to prepare a set of thermal barrier coating specimens, and water-cooling method was used in thermal shock experiments.
高温磨损机理为氧化物疲劳剥落磨损,精铸热锻模具钢磨损磨屑为厚大块状,而H13钢磨损磨屑以条状为主。
The high temperature wearing was due to the fatigue delamination of the oxide, the lump wear debris were revealed on the precision cast steel, and the bar wear debris on H13 steel.