分析了工厂网带炉条件下淬火织针表面硬度不足的原因。
Analyse the reason that surface hardness of quench needle is not enough under original production technology circumstance of factory.
严重的碳化物带状偏析,使拉刀产生局部淬火过热和回火不足,造成内应力急剧增高,最终导致拉刀断裂。
It was found that the broach was locally overheated due to band segregation of carbide, and under-tempered. These factors caused fracture of broach as a result of high internal stress.