结果表明,沿一次晶晶界的成分偏析对裂纹扩展阻力的降低作用是铸钢中贝壳状断口形成的主要原因。
The results show that main cause of conchoidal fracture forming is that composition segregation in solidification grain boundary of casting steel reduces the resistance of crack propagation.
着重于初生晶种制备工艺参数的试验研究和二次晶种存在的探讨;
The technological parameters for making first crystal seeds and the influence of existence of secondary seeds have been studied.
指出在一定限度内,随硅含量增加,铸坯的一次晶间距加宽,各类低倍组织缺陷大大减少。
Within specified limits, the primary dendrite spacing will be extended and the macrostructure defect will be obviously decreased in continuous cast billet with the increase of silicon content.