结果表明,焊缝金属中存在的非金属夹杂物,在低应力作用下形成微裂纹成为裂源,加之焊缝组织中存在大量的M A结构群,从而发生焊缝金属在室温下的解理断裂。
The results showed that nonmetallic inclusions in weld seam served as crack initiation site under external bend load, and large amount of m a structure resulted in cleavage fracture of weld seam.
疲劳断裂的主要原因是在材料中存在的夹杂物诱发裂纹源,在循环应力的作用下裂纹扩展导致断裂。
The main course of fatigue fracture is due to existence of the inclusion in the material. The inclusion induce crack initiation, the crack propagation and the axe fracture in the circle stress.