介电损耗是指电介质在交变电场中,由于消耗部分电能而使电介质本身发热的现象。原因,电介质中含有能导电的载流子,在外加电场作用下,产生导电电流,消耗掉一部分电能,转为热能。表示绝缘材料(如绝缘油料)质量的指标之一。
...介电损耗,德拜弛豫,激活能 [gap=1406]KEY WORDS: high dielectric material, CaCu3Ti4O12,dielectric constant, dielectric loss,Debye relaxation, activation energy ...
基于796个网页-相关网页
... 介电常数Dielectric constant 介电损耗Dielectric loss tangent 固化条件Curing conditions ...
基于42个网页-相关网页
...介电损耗;居里温度 [gap=1396]llic material; BaSrTiO3 dielectric ceramics; CeO2; relative dielectric constant; dielectric loss factor; Curie temperature ..
基于20个网页-相关网页
介电损耗角 dielectric loss angle
介电损耗常数 [电] dielectric loss constant
介电损耗因子 [电] dielectric dissipation factor
低介电损耗玻璃 low-loss glass ; low dielectric-loss glass ; low dielectric-loss glass low-loss glass
介电损耗角正切 dielectric loss angle tangent ; dielectric dissipation factor ; tangent of dielectric loss angle
介电损耗率 dielectric dissipation fraction
介电损耗因数 Dielectric Dissipation Factor
内部介电损耗 internal dielectric loss
The bulk density of this material is 2.71 g/cm3, the bending strength is 120MPa, the dielectric constant and the dielectric loss at 1MHz are 8.6 and 1.27×10-3 respectivly.
烧结试样的体积密度为2.71g/cm3,抗弯强度为120MPa;在1MHz的测试频率下,其介电常数为8.6,介电损耗为1.27×10-3。
参考来源 - CBS/AlWhen the heat-treatment temperature is 650 C,the tangent of dielectric loss angle of the fiber approachs to 1, and the frequency response characteristic is fine from 2GHz to 18GHz .
经过650℃热处理的纤维,介电损耗角接近于1,在2GHz—18GHz频率范围内具有较好的频响特性。
参考来源 - PAN基吸波纤维和吸波结构的研究·2,447,543篇论文数据,部分数据来源于NoteExpress
结果表明:极化后的介电常数和介电损耗低于极化前。
It was found that the dielectric constant and dielectric loss of unpoled samples is higher that those of poled samples.
CCL的介质性能主要是指介电常数、介电损耗和介质厚度。
Dielectric property of CCL embody dielectric constant, dielectric lose and dielectric thickness.
复合材料的介电常数和介电损耗随pani含量的增加而上升。
The dielectric constant and dielectric loss of the composites rise with increasing the content of PANI.