干压成型是指陶瓷生产中较常用的一种坯体成型方法。将粉料加少量粘合剂造粒,然后装入模具中,在压力机上加压,使粉粒在模具内相互靠近,并借内摩擦力牢固地结合,形成一定形状的坯体。感应加热表面热处理。
Die pressing process and cold isostatic pressing process are the important methods of making ceramic parts.
陶瓷粉末干压成型和冷等静压成型是制备陶瓷结构部件的重要方法。
参考来源 - 陶瓷粉末压制成型过程数值模拟的研究In this paper,The RBSC ceramics had been prepared by dry pressing with 3.5μm SiC,which tonerdensity of 0.91g/cm~3 and exhibit density of 3.16g/cm~3;The RBSC materials get the fracture strength 594MPa by In-situ solidification forming.
本文采用干压成型法用3.5μmSiC粉制备出素坯碳密度为0.91g/cm~3,烧结密度为3.16g/cm~3的高密度RBSC材料;采用原位凝固成型法制备出断裂强度为594MPa的RBSC材料。
参考来源 - 低温反应烧结制备碳化硅陶瓷材料及其结构与性能研究·2,447,543篇论文数据,部分数据来源于NoteExpress
本文对硅酸盐制品半干压成型制度进行探讨;
The paper describes a study on semi—dry pressing process for calcium silicate brick.
同时,对干压成型中不同粘合剂的作用效果进行了比较。
The effects of the different bonds for die pressing forming were compared as well.
该粉具有良好的流动性及快速填充性,可直接用于干压成型。
This powder is of well flowing property and fast-packing property, and can be directly made into shape by dry compaction.