结合扫描电镜(SEM)及能谱(EDS)分析,采用电化学阻抗谱、极化曲线测试以及丝束电极(WBE)技术,对黄铜电极在含硫酸盐还原菌(SRB)的模拟冷却水中表面成膜及腐蚀状况进行了分析。
基于39个网页-相关网页
...的锌/钢电偶腐蚀行为 - TNMSC 关键字: 丝束电极;镀锌层;电偶腐蚀;阴极保护;氢析出[gap=1541]Key words: wire beam electrode; zinc coating; galvanic corrosion; cathodic protection; hydrogen evolution..
基于10个网页-相关网页
The experimental results showed that the wire beam electrode could be used to study inhomogeneity of localized corrosion of metals.
结果表明,采用丝束电极技术能较好地研究金属局部腐蚀的不均匀性。
参考来源 - 用丝束电极研究缓蚀剂对金属局部腐蚀的影响·2,447,543篇论文数据,部分数据来源于NoteExpress
采用丝束电极研究防锈油膜失效之前的电位变化。
Potential variation of rust preventing oil film after its degradation was studied by using wire beam electrode.
采用丝束电极,对涂油金属的电化学不均匀性进行了研究。
The electrochemical inhomogeneity on oil painted metal was studied by wire beam electrode.
结果表明,采用丝束电极技术能较好地研究金属局部腐蚀的不均匀性。
The experimental results showed that the wire beam electrode could be used to study inhomogeneity of localized corrosion of metals.