... flash welding 火花〔电弧,闪光〕焊,电弧对焊接 weld porosity 焊缝气孔;焊缝气孔,焊缝孔隙 bevel weld 坡口焊缝,铲边焊缝;斜角焊缝 ...
基于140个网页-相关网页
... flash welding 火花〔电弧,闪光〕焊,电弧对焊接 weld porosity 焊缝气孔;焊缝气孔,焊缝孔隙 bevel weld 坡口焊缝,铲边焊缝;斜角焊缝 ...
基于14个网页-相关网页
porosity in weld 焊缝内砂眼
porosity in the weld 焊缝中气孔
weld zone porosity 焊区气孔
weld metal porosity 焊缝气孔
The common welded defects in the joints are oxide slag,porosity,cracks,etc. The occurrence of weld porosity and cracks could be reduced by removing the oxide film,dirt and oil completely before welding,strengthening the protection for welding pool,etc.
试验过程发现:AZ31镁合金TIG焊和等离子弧焊接时存在的主要缺陷都是气孔和热裂纹,对工件表面的氧化膜和油污进行处理,加强对焊接熔池的保护等工艺措施,可以有效减少焊接气孔和焊缝裂纹的产生。
参考来源 - AZ31镁合金非熔化极气体保护焊工艺及性能研究·2,447,543篇论文数据,部分数据来源于NoteExpress
On the contrary, it will create weld porosity and poor formation.
弧长太长会产生气孔及焊缝成形差等焊接缺陷。
Recognizing that the solubility of gas is greater in the liquid state than in the solid state, the subject of weld porosity is relevant to fusion zone discussion.
认识到溶解度的气体是更大的,在液体状态,比在固体状态下,受焊缝孔隙率是相关的熔合区的讨论。
Stick Welding Porosity in a weld is considered poor quality.
棒焊接的焊缝气孔被认为是质量差。