Despite continuing improvements in resin-based composites,polymerization shrinkage remains a major drawback of polymerizable resins. Polymerization shrinkage generates stress within the composite that may lead to marginal gap formation,microleakage,postoperative sensitivity and secondary caries.
尽管树脂材料不断改进,仍然具有聚合收缩的缺陷,树脂聚合收缩常导致边缘微渗漏和裂隙的形成,这样就易于产生术后敏感和继发龋。
参考来源 - 流动复合树脂用于后牙Ⅱ类洞龋损树脂修复的基底层的研究·2,447,543篇论文数据,部分数据来源于NoteExpress
CONCLUSION: Polymerization shrinkage of composite resin has negative effect on bonding strength of adhesives.
结论:树脂固化时的体积收缩可在黏结层产生较大的应力,影响黏结强度。
Polymerization shrinkage of resin composites is a major obstacle to their clinical success as dental restorative materials.
在临床中,牙体修复材料的固化收缩是造成牙体修复失败的主要原因。
Polymerization volume shrinkage of EEPE resin was lower than other dimethacrylate resin.
与其他甲基丙烯酸类树脂相比,EEPE树脂的聚合收缩率比较低。