The results show that the axle has defects in heat treatment, which leads to micro crack in early stage of service life and the extended crack finally causes fatigue fracture.
结果表明,该轴热处理上存在的不合理之处,导致轴在服役早期出现微裂纹,部分微裂纹在工作应力的作用下疲劳扩展,最终产生疲劳断裂。
The effect of re modification and heat treatment on formation of thermal fatigue crack in low chromium wear-resistant cast iron was investigated.
研究了稀土变质及热处理对低铬耐磨铸铁热疲劳裂纹形成的影响。
Heat treatment process has no effect on the propagation mode of thermal fatigue crack and the shape of crack at the sample notch.
热处理工艺对裂纹在试样缺口处的形态及裂纹的传播方式无影响。