Ternary boride based cermet cladding material was prepared by in situ reaction and liquid phase sintering technology in vacuum furnace.
在真空烧结炉中通过原位反应液相烧结工艺制备出三元硼化物基金属陶瓷覆层。
The results show that interface element diffusion and reaction on interface in vacuum hot-pressing sintering processing improved interface strength. Fracture occurred mainly in Al matrix.
结果表明,真空烧结过程中出现了界面反应,改善了界面结合强度,断裂破坏主要在基体上进行。