impact corrosion wear 冲击腐蚀磨损
impact-corrosion-wear 冲击腐蚀磨损
impact-corrosion-wear property 冲击腐蚀磨损性能
impact corrosion wear property 冲击腐蚀磨损性能
Results show that the leading mechanisms of both alloys are shallow flaking under 2.0 J impact work, and the anti-impact-corrosion wear are close.
结果表明,2.0 J冲击功条件下,中碳合金钢、低碳高合金钢均以浅层剥落为主,抗冲击腐蚀磨损性能相近;
Engineering ceramics feature resistance to high temperature, corrosion, wear and hot impact.
工程陶瓷材料具有耐高温、耐腐蚀、抗磨损及抗热冲击等优点。
The influence of impact energy on the synergy and the mutual effect mechanism between corrosion and wear were discussed.
最后探讨了冲击载荷下磨损与腐蚀的交互作用机理,以及冲击功对交互作用机理的影响。