The variety of surface morphology of the coatings in different Cr target current was observed. Some significant results are obtained as follows: The C-C bond structure of Cr-containing graphite-like carbon coatings is mainly sp2.
结果表明:本文制备的含铬类石墨碳膜的C-C键合结构以sp2为主。