Parameters of stress exponents and deforming activation energies,which characterize the deformation capability and microstructure evolution,were calculated through analysis hot deformation behavior of the alloy. On the basis of the above,constitutive relation for hot deformation of the alloy were established.
通过分析该合金的热变形行为,获得了应力指数、应变速率敏感指数和热变形激活能等表征其变形特性的重要特征参数,并采用所得参数建立了热变形本构关系。
参考来源 - TC11钛合金热变形特性分析及其本构关系的建立·2,447,543篇论文数据,部分数据来源于NoteExpress
结果表明:组织特征对合金的热变形行为有显著影响。
The results show initial microstructure characteristics have significant influences on the hot deformation of alloys.
采用单道次压缩试验,研究了变形温度和变形速率对SS400钢热变形行为的影响。
Effects of SS400 steel's deformation temperature and strain rates on its deformation behavior was studied using single pass compressing test.
采用等温热压缩试验对一种自行研制的高强度易切削锌基合金进行热变形行为的研究。
The hot deformation behavior of a self-developed zinc based alloy was investigated by isothermal compression test.