细晶Mo-40%Cu合金的烧结性能 - 中南大学学报(自然科学版、英文版) 关键字: Mo-Cu合金;烧结性能;致密化[gap=1226]Key words: Mo-Cu alloy; sintering characteristics; densification
基于16个网页-相关网页
铁矿石烧结性能预报模型 - 中南大学学报(自然科学版、英文版) 关键字: 铁矿石;烧结性能;神经网络;建模;预报[gap=1051]Key words: iron ore; sintering capability; neuralnetwork; modeling; predictio
基于6个网页-相关网页
. The result indicates that the synthetic temperature of mullite decreases notably (<1350℃) with the content of Al powder increasing, however sintering performance for the ceramic deteriorates at the same time.
结果表明,当Al粉含量增大时,莫来石的合成温度显著下降(﹤1350℃),但烧结性能也随着下降。
参考来源 - 氧化物陶瓷宏观裂纹的修复The results show that the sinterability was advanced by the second phase. While the sintering temperature at 1900℃and the gas pressure of 8Mpa, the relative density of 96% was obtained by adding 50wt%Al_2O_3.
结果表明第二相的加入在一定程度上改善了材料的烧结性能,在1900℃、压力8MPa的条件下,加入50wt%Al_2O_3,烧结体的相对密度为96%。
参考来源 - TiBGenerally, the W-Cu composite powders fabricated by conventional methods have poor sinterability.
传统方法制备的钨铜复合粉末的烧结性能较差。
参考来源 - 机械合金化法制备WThe effects of dopants Bi2O3、Sb2O5、MnO2 and glass phase on the properties of the ANT and ANNT system were investigated. It suggested that proper doping could improve the sintering properties and dielectric properties of the system.
详细研究了改性添加剂Bi2O3、Sb2O5、MnO2以及玻璃相对该系统介电性能的影响,研究表明适当的的掺杂可以有效改善系统的烧结性能和介电特性。
参考来源 - 新型超高介高频热稳定中温烧结瓷料研究Oxalate co-precipitation method was employed to prepare ultra-fine CGO powders. The properties of the powders, including the phase composition, morphology, as well as sintering ability were characterized.
首先,采用草酸盐共沉淀法制备CGO电解质粉体,并对材料的合成与制备工艺,粉体的微观结构、微观形貌,烧结体材料的形貌及烧结性能等进行研究。
参考来源 - 复合电解质(CGO)·2,447,543篇论文数据,部分数据来源于NoteExpress
采用分段反应烧成制度可以提高试样烧结性能。
The sintering properties of specimens can be improved by staged reaction sintering.
材料的烧结性能受材料中莫来石化行为所制约。
The sinter property of materials depends on its mullitization behaviour.
比较了这两种复合材料的结晶性能和烧结性能。
Sinterability and crystallization behavior of the two types of ferrite composites were compared.