表面碳势为1.1%C的渗碳硬化层内,临近外表面部位的枣核马氏体中会出现显微裂纹。
When carburized under high carbon potential (1. 1% C), microcracks tend to appear on the martensitic matrix near the outer surface of the layer.
试件的疲劳断裂模式全部为双面穿板断裂,疲劳裂纹起始于点焊热影响区搭接板内表面,沿板厚方向向外表面扩展;
Fatigue specimens cracked at two-sided through-thickness sheet, fatigue crack appeared initially in HAZ of inner surface of lap plates, along the thickness direction extended to outer surface;