...固化收缩率;体积电阻率[gap=1271]Key words: electrically conductive adhesive; epoxy resin; curing agent; curing shrinkage; volume resistivity...
基于28个网页-相关网页
·2,447,543篇论文数据,部分数据来源于NoteExpress
选用三种不同固化收缩率的基体树脂和两种银粉,分别配制了六种导电胶。
Based on two kinds of silver powder with different morphology and three matrixes with different curing shrinkage, six electrical conductive adhesives were prepared.
本文对MFE环氧乙烯基酯(含mfe型和afe型二种型号)树脂的固化性能(凝胶时间、放热峰和固化收缩率)作了报道并进行讨论。
The curing characteristics such as gel time, heat Peak and curing shrinkage rate of MFE epoxy vinyl ester resin (MFE type and AFE type) are discussed in this paper.
结果表明,在不饱和聚酯树脂中加入2 0 %的该类低收缩添加剂,树脂的固化收缩率为2 1% , 弯曲强度保有率为88% ,弯由模量没有明显变化;
It shows that after adding 20% low profile additive to the UP resin, the shrinkage rate of cured resin is 2.1%, the retention rate of bending strength is 88% and no change in flexural modulus.