采用间接开环聚合法合成了平均分子量为444 ,848的聚乳酸,并对合成工艺作了优化。
The of polylactic acid(PLA) was obtained by ring-opening polymerization and the synthesis conditions to get 444,848 molecular weight were optimized.
采用最优化工艺合成的液体树脂残碳量达到49%。
The remaining carbon of the liquid resin is 49% by adopting best technology.
结果表明:通过优化反应条件,使得在苯溶剂中合成出的聚L-乳酸的粘均分子量可达到232,000。
The result shows the viscosity-average molecular weight of poly(L-lactic acid) attains to 232,000 synthesized by optimizing the reactive conditions.