超支化聚合物的玻璃化转变温度随分子量的增加先增大,当分子量足够大时玻璃化转变温度不再受其影响。
The glass transition temperature of hyperbranched polymers rises with the increase of molecular weight. When the relative molecular mass was high enough it remained the same.
结果表明:随渗透率级差的增大,残留聚合物再利用提高采收率幅度先增加后减小;
The results indicate that with the permeability ratio increases, the enhanced recovery rate of residual polymer reutilization presents a first increases and then decreases trend;
研究结果表明,聚合物涂膜的拉伸强度随UPA和EGDMA用量的增加均呈现先增大后减小的趋势;
The experimental results show that the tensile strength of emulsion films firstly increases and then decreases with the increase of the UPA and EGDMA dosages.