The result shows that adhesive content is vital, but unit press and temperature and time of hot press are minor to the variance of warp degrees.
研究表明:涂胶量的影响显著,热压温度、热压时间和热压压力的影响不显著。
When the modified neoprene or polyurethane adhesive content in UHMWPE fibers was 6%, the strength of UHMWPE fibers increased 17.2% or 13.9%, respectively.
纤维表面漫胶处理后断裂强力提高,当UHMWPE纤维中改性氯丁胶或聚氨酯粘结剂的含量为6%时,其断裂强力增加17.2%或13.9%。
The experimental expression on the resistivity of carbon copper composite change with copper content in carbon copper mixture powder and adhesive content was decluced.
回归分析表明,粘结剂加入量对复合材料电阻率影响较大,碳铜混合粉含铜量对复合材料电阻率的影响较小。