采用体视显微镜、扫描电镜等分析手段对K18合金增压器涡轮铸造叶片的断裂形貌与断裂机制等进行了分析。
By means of stereomicroscopy and scanning electronic microscopy (SEM), the fracture mode and mechanism of the broken K18 superalloy cast blade in a supercharger turbo were investigated.
结果表明:增压器喷嘴环和涡轮叶片流通面积减少是涡轮增压器喘振的主要原因。
The results show that the reason why surge happened is that flow area of nozzle ring and blade was decreased.