高吸油性树脂的结构特点是:高分子之间形成一种三维的交联网状结构,材料内部具有一定微孔结构。
The structure of the high oil adsorbing resin is characterized by a three dimension crosslinked network structure among the high molecula, and there is a porous structure inside the resin.
考察了聚合温度、单体、交联剂和溶剂萃取树脂对高吸油性树脂吸油性能的影响。
The effect of polymeric temperature, monomers, crosslinking agents and solvent-extraction on absorbency of high oil-absorbent resin were investigated.
以甲壳素为原料,采用正交试验法确定制备高脱乙酰度和高交联度的壳聚糖树脂的工艺条件。
For preparing chitosan resin of high deacetylation degree and high cross-linking degree, chitin is taken as raw material and orthogonal test is adopted to determine technological condition.
研究了共聚单体的配比、交联剂用量、引发剂用量诸因素对高吸油性树脂的性能影响。
The effects of the amount of initiator, crosslinker and monomer composition on the oil absorption capacities of copolymer were studied.
对不同条件下制得的高交联大孔苯乙烯-二乙烯苯树脂的吸附性能进行了研究。
The adsorption behaviour of highly crosslinked macroporous resins prepared under different conditions was investigated.
用不饱和氨基甲酸酯、丙烯酸异辛酯和交联剂,以悬浮聚合的方法制备高吸油性树脂。
Useing unsaturated urethane, 2-ethylhexyl acrylate, crosslinking agent, high oil-absorbent resin was prepared by suspension polymerization.
这类聚合物的双叠氮交联剂组成的负型感光树脂具有高感度,高分辨率,稀碱水显影以及优良的抗蚀性能。
Some of the negative photopolymers composed of these polymers and bisazides can be developed in dilute aqueous base easily and clearly with excellent performance on photosensitivity and residual film.
采用悬浮聚合法合成甲基丙烯酸酯类高吸油树脂,研究了交联剂、引发剂用量对树脂性能的影响。
The oil-absorption of high oil-absorption resin, as an emerging technique to remove oil in environment, is causing widespread concern.
采用悬浮聚合法合成甲基丙烯酸酯类高吸油树脂,研究了交联剂、引发剂用量对树脂性能的影响。
A high oil-absorption resin of polyacrylic acid system with moderate crosslinking was synthesized by suspension polymerization.
研究了共聚单体的配比、交联剂用量、引发剂用量诸因素对高吸油性树脂性能的影响。
The effects of amount of initiator, crosslinking agent used and monomer composition on the oil absorption capacity of copolymer were studied.
以丙烯酸 2 -乙基己酯与醋酸乙烯酯为单体 ,采用悬浮聚合法 ,以单体自交联制得高吸油性树脂。
The high oil-absorption resin of copolymer of vinyl acetate and (2-ethylhexyl) acrylate was prepared by suspension polymerization with self-crosslinking.
用于有机合成、树脂改性、高吸收剂的交联剂、离子交换树脂的中间体等。
Used in organic synthesis, resins, high absorbent crosslinking agent and intermediates of ion exchange resin, etc.
用于有机合成、树脂改性、高吸收剂的交联剂、离子交换树脂的中间体等。
Used in organic synthesis, resins, high absorbent crosslinking agent and intermediates of ion exchange resin, etc.