通过SEM和XRD分析了黑色陶瓷膜层的微观形貌和相结构。
Morphology and phase structure of the black ceramic coatings were also investigated by XRD and SEM.
该方法所得陶瓷膜层光滑平整,具有好的耐磨性及抗高温氧化性。
The ceramic coatings obtained are smooth and level, and have good wearability and resistance to oxidation at high temperature.
该方法所得陶瓷膜层光滑平整,具有好的耐磨性及抗高温氧化性。
The ceramic coatings obtained are smooth and level, and have good wearability …
采用常压CVD方法在铝合金基底上制备出硅氧化合物陶瓷膜层。
The silicon oxide films on aluminum alloys matrix were prepared by chemical vapor deposition (CVD) in ambient pressure.
并测量陶瓷膜层的厚度,观察膜层微观形貌,通过盐雾试验来评定陶瓷膜层的耐蚀性。
The thickness of ceramic film was measured, the morphology of film was observed, the corrosion resistance of ceramic film was determined through salt-fog test.
本研究采用常压化学气相沉积(CVD)的方法在金属铝基底上制备出硅氧化合物陶瓷膜层。
A new kind of silicon oxidic film on aluminum was prepared by chemical vapor deposition (CVD) in ambient pressure.
通过这种技术可在铝合金表面获得高硬度、高热抗、耐腐蚀性好、附着力高、色泽稳定的陶瓷膜层。
A film with excellent hardness, heat resistant, corrosion resistance, adhesive power and color can be prepared by said micro-plasma oxidation technology.
并且陶瓷膜层耐蚀性在过电压为100 ~ 150V时较好,因此镁合金微弧氧化要选择适当的过电压。
When the over-voltage is 100 ~ 150 v, the ceramic level corrosion resistance is good. Therefore, the micro-arc oxidation of Mg alloy should choose the suitable over-voltage.
在钛合金表面用微等离子体氧化能产生一层陶瓷膜。
A layer of ceramic film can be grown on ti alloy by the micro plasma oxidation.
观察、分析了镀铝层表面微弧氧化陶瓷膜的微观形貌以及组织结构;
The morphology and the structures of the micro arc oxidation ceramic layer was observed and analyzed.
研究了ADC12铝合金表面微等离子体氧化法制备黑色陶瓷膜的电解液成分和电参数等对膜层性能的影响。
Influences of main parameters such as composition of electrolyte and electrical parameters in preparing black ceramic coating by microplasma oxidation on ADC12 aluminum alloy were studied.
微弧氧化技术是将铝合金置于电解液中通电使其表面产生微弧放电,而在铝合金表面原位生长一层陶瓷膜的表面处理技术。
It is a technology that ceramic film is formed in condition of hyperthermia and heavy pressure produced by micro-plasma on aluminum alloy in given electrolyte.
为提高钛合金的耐腐蚀性能,在其表面用微等离子体氧化法生长一层陶瓷膜。
A layer of ceramic film is produced by micro plasma oxidation on the surface of ti alloy in order to improve its corrosion resistant property.
经一定的腐蚀时间后,微弧氧化陶瓷膜的多孔层最终遭到破坏,而紧密层对防腐蚀起着至关重要的作用。
The outer porous layer is damaged after corrosion, while the inner dense layer played a key role to protect the coating from corrosion.
结果表明:采用三种不同波形均可在镁合金表面得到一层光滑致密褐色系列的类陶瓷膜。
The results show that a series smooth and dense brown ceramic films layer can be obtained by using these waveforms.
所述的纺织机械用纺杯,其基体采用铝基材料制造,在纺杯基体工作表 面设置有一层陶瓷膜。
The base body of the textile cup for textile machinery is made of aluminum-based material, and a layer of ceramic membrane is arranged on the working surface of the base body of the textile cup.
该致动器的多层膜压电元件由流延法或丝网印刷工艺等制作压电陶瓷膜,采用丝网印刷工艺等制作中间电极层。
It makes piezoelectric ceramic film by casting method or web printing technique, etc., and makes medium electrode layer by web printing technique, etc.
结果表明,陶瓷膜具有内部致密层和外部疏松层两层结构,膜层与铝基体为冶金结合。
The results show that the ceramic coating is composed of a two-layer structure with the surface loose zone and the inner compact zone.
结果表明,陶瓷膜具有内部致密层和外部疏松层两层结构,膜层与铝基体为冶金结合。
The results show that the ceramic coating is composed of a two-layer structure with the surface loose zone and the inner compact zone.