钢锭的浇铸通常是在氩保护下进行的。
Teeming (pouring) of ingots is done usually under argon protection.
简述了钢锭断面形状对厚板成材率的作用。
This paper describes the effect of ingot cross section on thick plate yield.
因钢锭模表面生成气体而形成的表面针孔。
钢锭缺陷广义上可分为内部缺陷和表面缺陷。
Ingot defects may be broadly classified into internal flaws and surface flaws.
调查分析了一些特殊钢厂的钢锭退火工艺规范。
The ingot annealing technology in some alloying steel plant have been investigated.
为避免此类缺陷产生,必须保证钢锭的浇注质量。
Keeping pouring quality would prevent the ingot steel from forging bursting.
探讨了链条清理圆柱钢锭模和矩形钢锭模的机理。
This paper researches into the mechanisms of chain cleaning machine for both cylindrical and rectangular steel ingot model.
提高钢锭的利用率是降低锻件成本的重要途径之一。
Increasing the utilization ratio of the steel ingot is an important way to reduce the forging cost.
由于这是融化我跑去找完成沉重的角铁焊大型钢锭模。
As it was melting away I hurried off to finish welding a large ingot mold from heavy Angle iron.
介绍了空心钢锭的清理生产规程和实际生产中存在的问题。
The production specification of cleaning process for hollow ingots and the available issues of actual production have been introduced.
你的意思是用不同特性的钢铸成的钢锭有不同的内部结构吗?
Do you mean ingots cast with steels of different properties have different interior structures?
指出钢锭馍焊补技术是提高钢锭模使用寿命的重要措施之一。
The ingot repairing welding technology being one of important measures improving ingot mould service life is put forward.
因此,在进行钢锭模设计时,应综合考虑钢锭的质量和成材率。
Therefore, both quality of steel ingot and yield are considered synthetically.
微渣池的形状和稳定性影响着钢锭渣皮厚度的变化和钢锭表面质量。
The shape and stability of the "miniature slag pool" affect the thickness of slag skin and the ESR ingot surface quality.
钢锭缺陷广义上可分为内部缺陷和表面缺陷。内部缺陷是因收缩引起的。
Ingot defects may be broadly classified into internal flaws and surface flaws. Internal flaws are caused by shrinkage.
我参观过传统的炼钢厂:巨大的高炉、转炉、钢锭,长达几英里的铁轨。
I have seen one of the conventional steelworks: huge blast furnace, converter, steel ingot, miles of railway track.
我参观过传统的炼钢厂:巨大的高炉、转炉、钢锭,长达几英里的铁轨。
I had saw one of the conventional steelworks: huge blast furnace, converter, steel ingot, mile of railway track.
为了减少镇静钢钢锭(坯)表面缺陷,出现了各种类型的保护浇铸技术。
A variety of protective casting process have been developed for decreasing defect on killed steel bloom sur-face.
结疤。通常由钢锭缺陷引起的、附着在完好金属表面上的薄壳状或镶片状缺欠。
Scab. An imperfection in the form of a shell or veneer, generally attached to the surface by sound metal. It usually has its origin in an ingot defect.
电渣熔铸过程中, 金属熔池深度直接影响熔铸件的结晶,从而影响钢锭的质量。
The depth of molten pool directly influences the crystallization of castings, thus influence the quality of ingots in the ESR.
铸锭时控制钢液的注流速度,是改善和提高钢锭表面和内部质量的重要工艺措施。
During ingot casting, control of casting speed is an important measure to improve the surface and inner qualities.
主要的铸锭设备有盛钢桶和钢锭模。盛钢桶是用来盛装从炼钢炉放出的钢液的容器。
The major equipments are the ladle and the mould. a ladle is a container to hold the molten steel tapped from the steel making furnace.
应用该程序计算了包钢B114钢锭模内冷却的温度分布和凝固率随时间的变化规律。
Using the program, the relation between ingot temperature, solidfying rate and solidfying time of B114 ingot are obtained.
分析了传统设计在大型钢锭模上的局限性,为采用计算机设计大型钢锭模提出新的思路。
The limitation of the conventional design of the heavy duty ingot mold has been analyzed in this article.
适用于磨钢锭、铸件打毛刺、石材表面精加工、切割、抛光等。但该类磨具不抗碱性溶液。
It is suitable for the grinding of steel ingot, removing burrs of casting, precision grinding of stones, cutting and polishing. But it should be kept away from alkaline solution.
对影响钢锭质量的主要成分的分析方法进行了研究,制定出了日常检验的系统的分析方法。
The analysis methods for primary slag compositions. influencing on ingot quality, have been researched, a systemic analysis method has been established for routine test.
对影响钢锭质量的主要成分的分析方法进行了研究,制定出了日常检验的系统的分析方法。
The analysis methods for primary slag compositions. influencing on ingot quality, have been researched, a systemic analysis method has been established for routine test.
应用推荐