淬火裂纹:裂纹在钢材的淬火或淬火后形成,由于冷却时的高应力所造成;也有可能是在淬火油中的水所导致。
Quench Cracks: Cracks formed in a steel part during or after quench, resulting from high stresses in cooling; could be caused by water in the quench oil.
淬火裂纹:裂纹在钢材的淬火或淬火后形成,由于冷却时的高应力所造成;也有可能是在淬火油中的水所导致。
Quench Cracks: Cracks formed in a steel part during or after quench, resulting from high stresses in cooling; could be caused by water in the quench oil.