单晶,通过化学腐蚀和金相显微镜研究了(101)晶面蚀坑的形貌、分布特征及其密度的大小。
The shape, distribution and density of etch pits on the (101) face was observed by metalloscope after chemical etching.
但是晶粒尺寸增大后晶界处因局部腐蚀电流密度增大将会在局部造成更深的腐蚀坑槽并降低耐候性;
The total quantity of corrosion surface defect is decreased due to the decrease of grain boundary energy with the increase of grain size and the atmospheric corrosion resistance is increased.
但是晶粒尺寸增大后晶界处因局部腐蚀电流密度增大将会在局部造成更深的腐蚀坑槽并降低耐候性;
The total quantity of corrosion surface defect is decreased due to the decrease of grain boundary energy with the increase of grain size and the atmospheric corrosion resistance is increased.