最后得出三轴织物复合材料的模量分量。
Then modulus of triaxial woven fabric composites is obtained.
本文研究了织物编织类型及树脂含量对碳织物复合材料力学性能的影响。
The effect of resin content and weaving type of the fabrics on mechanical properties of carbon fabric reinforced composites was studied.
在整体化制造方面,研制和验证了织物复合材料正弦波梁的液态成型制造技术。
For integrated aircraft structure, sine wave beams were fabricated and demonstrated by using the textile fabrics and liquid molding.
将碳纤维织物浸渍-涂层酚醛-缩醛粘结剂树脂,加压固化后制备出碳纤维织物复合材料。
The carbon fabric composites were prepared by dip-coating of the carbon fabric in a phenolic resin and solidified under pressure.
本文应用能量原理和阻尼分析的方法解决了平纹织物复合材料的复杂结构损耗因子的计算问题。
The amplitude frequency characteristic curve and loss factor of laminated damping steel sheet have been calculated and measured with the sine scanning excited method.
论述将纳米复合材料通过浸渍涂层的方法整理到棉织物及服装产品上,使其具有抗紫外线性能。
This paper is related to the method of coating cotton fabric and apparels by used of the nano composite materials for the UV blocking function.
采用挤压铸造法制备出二维碳纤维织物增强镁基复合材料,并对其基本性能进行了研究。
Two dimensional carbon fiber fabric reinforced magnesium matrix composites were prepared by squeeze casting technology, and their basic properties were studied.
这种织物被用作热塑性纺织增强复合材料模件的预型件。
The fabric is used as a preform for thermoplastic textile-reinforced composite modules.
这种织物被用作热塑性纺织增强复合材料模件的预型件。
The fabric is used as preform for thermoplastic textile - reinforced composite modules.
多层机织物作为纺织复合材料的增强体有着广泛的发展前途,特别是在军工、航空等产业用纺织品领域应用广泛。
As reinforcement in textile composites, multi-layer woven fabrics have bright developing room, especially in industrial textiles field such as military industry, aviation and so on.
丁基橡胶胶乳是电线、电缆及涂层织物和复合材料的极好绝缘材料。
In latex form it is an excellent insulating material for wires and cables, as well as for coating fabrics and composites.
集圈联接的纬编间隔织物是一种具有一定厚度的针织产品,可以用作增强复合材料的底布。
The weft knitted spaced fabric is a kind of knitwear with a certain thickness. It can be used as a base structure for the fiber reinforced composite material.
论述了国内外碳纤维及其织物、预浸料、 复合材料的测试方法及标准化,供国内有关测试单位及专业技术人员参考。
The testing method and standardization of carbon fiber and its fabric, prepreg, CFRP are illustrated both at home and abroad, for some testing units reference.
研究了二维织物和针刺毡等纤维排布方式对复合材料显微结构和物理以及力学性能的影响。
The dependences of the microstructure and other properties of the composites on the distribution manner of fiber such as both 2d fabric and needle punching felt were investigated.
结果表明,复合材料的变形性能与增强纤维的含量,织物的组织结构及参数,拉伸方向等因素有关。
The experiment results indicate the deformation properties of composites are affected by fiber volume fraction, fabric structure and parameter, tensile direction etc.
本文对多向无皱褶纤维织物及复合材料的结构与性能进行了分析,并与传统的方格布等织物及复合材料进行对比。
The structure and properties of multiaxial non-crimp fabrics and composite are discussed, the comparison with traditional woven fabrics is also carried out in this paper.
文章利用玻璃纤维编织一种新型双轴向增强纬编间隔织物,并制作了该种结构的织物增强复合材料。
A new kind of biaxial spacer weft-knitted fabric was knitted using glass fiber, and then its reinforced composite was manufactured.
结果表明,组合式3d机织物增强复合材料具有接近正交3d机织物增强复合材料的弹性模量和抗拉强度。
The results show that the Young's modulus and tensile strength of the combinational 3d woven fabric reinforced composite are close to that of the 3d orthogonal woven fabric reinforced composite.
织物有两个外层,用U形或V形交连结构连接而成,主要应用领域为轻质复合材料。
These fabrics have two outer surfaces connected together with U and V shaped knitted cross-links which are particularly developed for the light weight applications.
本文综述了纬编针织物增强复合材料的特点与应用,结构与加工,以及在力学性能等方面的研究进展。
This paper summarizes characteristics, applications, structures and fabrications of weft knitted fabric reinforced composites and some research results of mechanical properties.
研究了两种不同预混法对织物预型件和复合材料浸润效果、拉伸性能和剥离性能的影响;
The effects of different premix technique on the effective infiltration, tensile and peeling properties of thermoplastic performs and composites were investigated.
仿形织物是制造高性能、净尺寸复合材料所必需的增强材料。
The woven fabric for shape weaving is an essential fiber reinforcement for making high performance and net shape composites.
目前,柔性复合材料的增强结构以机织物和经编双轴向织物为主。
In the present market, the reinforced part of the flexible composites are mostly woven fabric and warp-knitted bi-axial fabric.
混编法直接制成织物状,在复合材料成型时,只需对现成的织物进行加工,工艺大大简化。
The flax yarns and PP multifilament were produced into fabrics by co-weave technique which could be directly handled during composites molding.
研究以涤纶经编多轴向织物为基布、表面复合聚氯乙烯压延薄膜制成的新型可作膜结构材料使用的织物增强柔性复合材料的拉伸性能。
This paper discussed a new coated fabric used for membrane, which is made by multi axial warp-knitted fabric of the PET fiber reinforcing PVC sheets.
在这样一个技术,一个复合材料挤出板材是由与织物材料基片材料一起。
In one such technique, a sheet of composite material is produced by extruding a base material together with a sheet of fabric material.
主要研究了正交三维织物增强热塑复合材料的成型工艺,即成型厚度、成型温度对其弯曲性能的影响。
The molding technique to influence flexure property of orthogonal 3D woven reinforced resin composite were studied from the aspects of molding thickness and temperature.
织物的成型能力对于复杂形状复合材料的加工和性能有着很大影响,因此,有必要对织物成型能力进行深入研究。
The forming of fabric has much effect on the production and performance of final composite with complex shape. Then the investigation of forming character of fabric is much of necessary.
再以预处理后的新酚树脂为基体、乙炔炭黑为导电填料、玻璃纤维织物为增强材料制备了导电复合材料;
The modified xylok resin was subsequently blended with glass cloth and acetylene black to generate a new conductive composite.
再以预处理后的新酚树脂为基体、乙炔炭黑为导电填料、玻璃纤维织物为增强材料制备了导电复合材料;
The modified xylok resin was subsequently blended with glass cloth and acetylene black to generate a new conductive composite.