水合肼溶液的化学腐蚀又加剧了空泡腐蚀。
The chemical corrosion by the hydrazine hydrate solution enhances cavitation corrosion.
叙述了水合肼蒸发器加热管的腐蚀情况与腐蚀特征,分析其腐蚀原因主要是空泡腐蚀。
This paper describes the corrosion behavior of heating pipe in hydrazine hydrate evaporator, and shows that the main mechanism is cavitation corrosion.
通过讨论海上石油钻井平台用管材空泡腐蚀失效的案例,研究管材空泡腐蚀的宏观特征和微观特征。
The macro and micro characteristics of vacuolar corrosion were studied; a failure case of vacuolar corrosion of petroleum pipe of seashore well-drilling rig was discussed.
采用空泡腐蚀与定位跟踪观察交替进行的方式,研究了灰口铸铁在自来水中空泡腐蚀过程的表面形貌演变。
The surface morphology progression of grey cast iron due to cavitation erosion induced by tap water has been studied carefully by cavitation corrosion test and SEM observation in turn.
采用空泡腐蚀与定位跟踪观察交替进行的方式,研究了灰口铸铁在自来水中空泡腐蚀过程的表面形貌演变。
The surface morphology progression of grey cast iron due to cavitation erosion induced by tap water has been studied carefully by cavitation corrosion test and SEM observation in turn.