在承受频繁的弯曲应力作用后,在其焊接热影响区萌生了裂纹源进而发生疲劳开裂。
In frequent bending stress condition, fatigue cracking occurred due to the cracking source had been initiated in welding heat affected zone.
在承受频繁的弯曲应力作用后,在其焊接热影响区萌生了裂纹源进而发生疲劳开裂。
In frequent bending stress condition, fatigue cracking occurred due to the cracking source had been initiated in welding heat affected zone.