通过单因素实验确定了导电胶的最佳配方:镀银铜粉填充量为70%、复合光引发剂用量为4%、热引发剂aibn用量为2%、偶联剂KH570用量为2.5%。
The optimal formula of the UV curable conductive adhesive gained from single factor test was as follows: Silver-plated copper powder 70%, complex photoinitiator 4%, AIBN 2% and KH570 2.5%.
考察了热引发方式和不同种类、浓度下的引发剂引发方式在苯乙烯的本体聚合中对聚合反应速率和产品的分子量及其分子量分布的影响。
The effects of initiators and thermal initiation on a reaction rate, molecular weight and molecular weight distribution of products in a mass polymerization of styrene were investigated.
差热扫描量热分析表明偶氮引发剂与纳米碳酸钙螯合后分解温度略有降低;
The results of differential scanning calorimetry (DSC) showed that the decomposition temperature of ACPA decreased when it was chelated onto the particles.
以环氧丙烯酸酯、活性稀释单体、光引发剂等为原料,制备UV固化涂层,对主要原料及固化后的涂层进行了热失质量分析。
The title UV curing coatings is prepared based on epoxy acrylate, reactive diluents and photoinitiator. The main raw materials and cured film are tested with TGA.
以环氧丙烯酸酯、活性稀释单体、光引发剂等为原料,制备UV固化涂层,对主要原料及固化后的涂层进行了热失质量分析。
The title UV curing coatings is prepared based on epoxy acrylate, reactive diluents and photoinitiator. The main raw materials and cured film are tested with TGA.