对其孔结构、表面结构、溶胀性能和热稳定性进行了详细研究。
The pore structure, surface property, swelling capacity and thermal stability of the copolymer beads were determined.
结果表明,所合成树脂在极性溶剂中的溶胀性能均比在非极性溶剂中好;
The results show that the swelling properties of the synthetic resins in polar solvents are better than those in nonpolar solvents.
基于一种新型聚电解质水凝胶及其与黏土杂化水凝胶的合成,考察了所得凝胶的溶胀性能。
A new polyelectrolyte hydrogel and its hybrid hydrogel with the Laponite clay were prepared, and their swelling properties were investigated.
本文主要研究了短纤维-氯丁橡胶复合材料的力学性能和耐热性能,并研究了其溶胀性能。
In this thesis, the physical and heat-aging properties of short fiber-CR composite were mainly studied, and the swelling properties of the composite were also studied.
DTA和溶胀试验表明PU/OM T纳米复合材料的热稳定性能和耐溶胀性能得到明显的改善。
DTA and swelling tests indicate the thermal stability and the solvent resistance of PU/OMT nanocomposites are apparently increased.
该文以尼龙短纤维为例研究了短纤维的不同用量及其粘合性能对短纤维- CR复合材料的力学性能和耐热老化性能的影响;并研究了尼龙短纤维- CR复合材料的耐溶胀性能。
A study was made on the influence of different contents of nylon short fibers and interface adhesion on physical properties, heat aging properties and swelling of short fiber-CR composites.
实验结果表明,膜的溶胀量及分离性能与共聚物的交联剂用量及膜的共混比有关。
The experimental results show that the swelling quantity and characteristics of the blended membrane are related to the dose of crosslinking agent and blend ratio.
利用XPS、ATR-FTIR等手段来研究DMF预溶胀涤纶经电晕放电处理后的表面结构性能。
The surface structural properties of DMF pretreated PET fabric treated by corona discharge are studied through XPS, ATR - FTIR.
通过改变加料顺序、溶胀时间及双相互穿等多步聚合方法,考察了动态力学和力学性能变化的规律。
Their dynamic mechanical and mechanical properties were investigated via changing feeding order and swelling time as well as using the method of multistage polymerization for interpenetration.
测试了共混膜的力学性能、脱水率和溶胀度。
The mechanical properties, dehydration ratio and swelling ratio are determined.
竹浆纤维因其加工方法不同,除吸湿能力优于竹原纤维外,其放湿速度慢、吸湿溶胀率小、耐热性能也比竹原纤维差。
The bamboo pulp fiber has worse properties of swellability, moisture absorption and liberation rate and thermal stability except hygroscopic capacity.
通过溶胀曲线测定、红外光谱分析、复阻抗分析等手段对材料的结构与离子导电性能进行了研究。
Tests of swelling curves, infrared spectra analysis and complex impedance analysis were carried out to understand structure and ionic conductive properties of the samples.
分析了橡胶在二甲醚中溶胀的化学机理,并选出具有不同极性的橡胶材料进行耐二甲醚溶胀及溶胀前后拉断强度、拉断伸长率、硬度等力学性能的对比试验。
Chemical mechanism of rubber expansion in DME was analysed, and different rubber materials were selected to test the expansion, the tensile strength, the elongation at break, and the hardness.
IPN水凝胶具有快速退溶胀速率及可逆溶胀-收缩性能。
All IPN hydrogels show a fast deswelling rate and reversible swelling-shrinking property.
研究了O型丁腈橡胶密封圈中腈基含量对其耐润滑脂性能的影响,讨论了不同性能润滑脂对丁腈橡胶的溶胀作用机理。
The resistance to lubricating greases of some O-ring NBR seals was studied in this paper. The swelling of NBR in different lubricating greases were discussed.
考察了PVA含量对共混膜成膜性、吸水率、溶胀度、离子交换容量、热稳定性、离子传导率及力学性能的影响。
The effects of PVA content on membrane preparation, water uptake, swelling degree, IEC, thermal stability, ionic conductivity and mechanical strength were all investigated.
研究发现,原料配比、溶胀时间、反应温度是影响EOHEC粘度性能的重要因素。
It was found that the mixture ratio, swelling time and reactant temperature had important effects on the viscous character of product EOHEC.
研究了上述两种微球的表观形态、粒径分布、溶胀性、载药性能和体外磁响应性。
Their surface morphology, size distribution, characters of swelling, adsorbability for drug-carried and magnetic response were studied.
SPPHES均质膜的含水率和溶胀率随着SPPHES的磺化度和温度的升高而增大,磺化聚合物显示了很好的尺寸稳定性和较好的热性能。
The water uptake and swelling ratio of SPPHES increased as the increasing of SD and test temperature. TGA indicated that SPPHES had good thermo-stability.
SPPHES均质膜的含水率和溶胀率随着SPPHES的磺化度和温度的升高而增大,磺化聚合物显示了很好的尺寸稳定性和较好的热性能。
The water uptake and swelling ratio of SPPHES increased as the increasing of SD and test temperature. TGA indicated that SPPHES had good thermo-stability.