高低温湿热试验箱。
电化学试验和湿热试验结果表明电解铝硅合金具有良好的耐蚀性。
The results of electrochemical experiments and moisture and hot experiments indicate that the electrolytic Al - Si alloy has excellent corrosion resistance.
利用湿热试验、盐水浸渍试验及电化学测试方法评价了膜的耐蚀性能。
The anticorrosive property of the conversion film was examined intensively by moisture and heating test, salt solution immersion test and electrochemical method.
采用SEM、电化学、以及盐雾试验和湿热试验等其它方法对封孔材料与效果进行了评价。
The sealing materials and sealing efficiency was studied by means of SEM. electrochemical salt spay test and hot-humid test.
并介绍其涂覆层经人工加速试验、耐盐雾试验和耐湿热试验的结果,以及在各种气候条件下,经一年的天然暴露试验结果。
Meanwhile it introduces the results of manual coating acceleration test, salt spray test, damp and hot resistance test and the natural exposed test for one year under the various weather conditions.
本文介绍了交变湿热室试验控制的新方法,采用了简化的模糊控制,提出了模糊前馈解耦法。
This paper presents a novel test and control scheme for environmental chamber. The simplified fuzzy controllers and fuzzy feedforward decouple method are introduced.
通过湿热老化试验,研究了APMOC纤维吸湿性能、拉伸强度、断裂延长率以及弹性模量随老化时间的变化。
The changes of moisture absorption properties, tensile strength, fracture elongation and elastic modulus of APMOC fiber with aging time were investigated through the hygrothermal aging test.
对国产汽车所用210种涂层试样进行了湿热带大气环境自然曝晒试验及人工加速老化试验。
Natural exposing tests in humid tropics atmosphere environment and accelerated ageing tests for 210 coat test samples of domestic automotives are carried out.
将黄铜片用上述三种溶液钝化处理后,通过湿热加速试验、硝酸点滴试验、盐水浸泡试验及电化学测试对耐腐蚀性进行了研究。
The corrosion resistance of samples after passivation is studied in the experiment by humid-air accelerated corrosion test, nitric acid titrating test and the brine dipping test.
摘要 :本试验旨在研究湿热环境对自由采食情况下生长育肥猪采食行为的影响。
Abstract : This experiment was conducted to investigate the effects of hot and humid environment on feeding behavior in growing-finishing pigs with ad libitum feeding.
试验期间牛舍最小湿热指数(THI)在72以上。
The minimum temperature humidity index (THI) was normally more than 72 during experimental period.
本文介绍了复合材料及防护涂层在湿热区海洋性气候条件下的耐腐蚀性自然环境试验情况,并对结果进行了分析。
This text introduce the situation of natural environmental anticorrosive test of composite materials and it's coat on the Marine climate condition. And analysis the result of test.
通过实物轧辊试样的连续变温氧化试验、恒温持续氧化试验和湿热氧化试验,研究了高速钢材质的氧化生长过程。
The oxidation process of HSS is studied based on roll specimen's continuous dynamic heat oxidation experiment, constant temperature oxidation experiment and moist heat oxidation experiment.
计算结果和试验结果吻合得较好,为后续的CFL/EP复合材料湿热残余应力的分析打下了初步基础。
Therefore, the residual stress in the CFL/EP composite can be studied on the basis of the above results.
本文详细介绍了涂层织物湿热空气加速老化的试验方法。
This paper introduced a testing method of accelerated ageing to determine the effect of heat and humidity on the age of coated fabric.
采用室内贮存试验、人工加速湿热老化试验和红外光谱法研究了硬质聚氨酯泡沫塑料在室内贮存条件下的老化机理。
The aging mechanism of rigid polyurethane foams at indoor storage conditions was investigated with indoor storage tests, accelerated hygrothermal aging tests and IR spectra.
系列恒温恒湿试验箱适用于工业产品恒定湿热的可靠性试验。
Constant temperature and humidity chamber for the reliability of industrial products Damp heat test.
用试验验证了胶粘剂在湿热老化试验中,试样分别处于转动状态和静止状态对试验结果的影响,用数理统计的方法处理数据,得到了明确的结论。
This paper presents the influence of exposure state of the adherend samples to theresults of Wet-heat aging test. With handling data by mathematical Statisticalmethod. We got an evident conclusion.
用试验验证了胶粘剂在湿热老化试验中,试样分别处于转动状态和静止状态对试验结果的影响,用数理统计的方法处理数据,得到了明确的结论。
This paper presents the influence of exposure state of the adherend samples to theresults of Wet-heat aging test. With handling data by mathematical Statisticalmethod. We got an evident conclusion.