另外,还对混合稀土的适宜加入量进行了试验。
Furthermore, the suitable dosage of mischmetal addition has also been tested.
研究了混合稀土氧化物对粘土砖和高铝砖性能的影响。
The result sho-tvs that mixed rare earth oxide fine powders can be obtained.
镧镨铈混合稀土(LPC)是新型专利成分的混合稀土。
Lanthanum praseodymium - cerium rare earth (LPC) was a patent composition.
本实验研究了添加混合稀土氧化物对釉面质量和性能的影响。
The influences of mixed rare earth oxide on the quality and properties of glaze were studied.
主要研究了采用ICP-AES法测量混合稀土金属中的硅含量。
The ICP-AES method to determine the silicon content of mixed rare earth is studied in the paper.
当混合稀土含量为3%时,催化剂的丙烷转化率和丙烯收率达到最佳值。
It was found that the propane conversion and propylene yield could reach the maximum, when the content of mischmetal was 3%.
在常规铸造条件下,向高锌镁合金熔体中加入适量混合稀土获得高锌镁合金。
The high zinc magnesium matrix composite was fabricated by adding mix race earth into the molten high zinc magnesium alloy using common casting.
用差热分析及热裂环法研究了锑和混合稀土对AZ31镁合金铸造性能的影响。
The effects of antimony and mischmetal on the casting properties of AZ31 alloy were investigated using the differential thermal analysis and hot tearing ring method.
发现铈能改善合金的阳极腐蚀性能,而镧及混合稀土均使合金的阳极腐蚀性能变差。
It was found that Ce may improve the anodic corrosion properties of the alloy, but La and misch metal may make its properties worse.
该方法能同时测定富铕混合稀土氧化物中多种非稀土元素的含量,提高了分析速度。
This method could determine many non-REE in enriched-europium mixture rare earth oxide at a time and it was a rapid method.
在铁镍部分代钴的基础上,采用常规硬质合金工艺,以不同的混合稀土添加量进行了实验。
The conventional producing process of cemented carbide was applied on the basis of replacing cobalt partly with iron and nickel and the mixed rare earth of different content was added.
研究了混合稀土中常见杂质锌、铁、镁对贮氢电极材料的贮氢性能、电化学性能等的影响。
The influences of the usual impurities of Zn, Fe and Mg in mischmetal on the hydrogen storage and electrochemical properties of a hydrogen storage electrode are investigated.
探讨在不同剂量农用混合稀土“常乐”的作用下,大鼠肝脏的形态、功能改变及其作用机理。
To probe the effects of different dose Changle on morphological change in the liver and their mechanism in rats.
这样的分为两种材质,锌- 5%铝-混合稀土合金钢丝、锌- 10%铝混合稀土合金钢丝。
This is divided into two kinds of materials, zinc -5% aluminum mixed rare earth alloy steel wire, zinc -10% aluminum mixed rare earth alloy steel wire.
这样的分为两种材质,锌- 5%铝-混合稀土合金钢丝、锌- 10%铝混合稀土合金钢丝。
This is divided into two kinds of material, aluminum zinc - 5% - mixed rare earth alloy steel wire, aluminum zinc - 10% mixed rare earth alloy steel wire.
所述的镁-镧铈中间合金是由配比为质量为80% 的镁锭与质量为20%的镧铈混合稀土制成;
The magnesium-lanthanum cerium interalloy is prepared by 80% by mass of magnesium ingot and 20% by weight of lanthanum-cerium rare earth compound;
在轻重混合稀土中能单独分离镧、铈、镨、钬、钪。本方法能用于分离、测定独居石中的稀土元素。
Lanthanum, Cerium, Praseodymium, Holmium and Scandium from a mixture of rare earth elements can also obtained, This method is being us...
在轻重混合稀土中能单独分离镧、铈、镨、钬、钪。本方法能用于分离、测定独居石中的稀土元素。
Lanthanum, Cerium, Praseodymium, Holmium and Scandium from a mixture of rare earth elements can also obtained, This method is being used in...
采用自制的实验装置研究了富铈混合稀土时ZL201A合金在凝固过程中的准固态力学性能的影响。
The influence of mischmetal on the mechanical properties and solid-liquid coexisting zone of ZL201A alloy during solidification has been investigated with equipment specially designed.
对纯镁及AZ 91 D镁合金中添加富铈混合稀土的收得率及其各元素含量的变化规律进行了研究。
Mischmetal absorptivity and its effects on the element contents in pure magnesium and AZ91D alloy were investigated.
高尔凡(锌铝合金),又分为锌- 5%铝-混合稀土合金钢丝和锌- 10% -铝混合稀土合金钢丝。
Gao Erfan (zinc aluminum alloy), and divided into zinc -5% aluminum alloy steel wire and zinc alloy -10% - mixed rare earth alloy steel wire.
采用常规铸造方法,向ZA155高锌镁合金熔体中加入适量富铈混合稀土获得了稀土合金化的高锌镁合金。
Rare-earth alloyed high zinc magnesium alloy was obtained by adding proper Ce-rich misch metals into high zinc ZA155 magnesium alloy under conventional condition.
试验结果表明,在配料中加入适量混合稀土氧化物对提高耐火制品的常温耐压强度和热震稳定性能是有益的。
The results show that a certain amount of the mixed rare earth oxide content in the batch can increase the cold compression strength and the thermal shock resistance of the bricks.
结果表明,添加的镧镨铈混合稀土只有少量固溶在镁基体中,绝大部分形成了稀土化合物,沿晶界呈网状分布。
The results indicate that most of the rare-earth element are concentrated along the boundary in network of metallic compound with a few solutioned into the Mg matrix.
结果表明,添加的镧镨铈混合稀土,只有少量固熔在镁基体中,绝大部分形成了稀土化合物,沿晶界呈网状分布。
The results indicated that a few of the rare-earth elements existed in the matrix, and most of that formed metallic composite with magnesium and distributed in the interface.
镁熔体对混合稀土存在着吸收极限,该试验条件下纯镁的吸收极限为1.6%左右,AZ91D合金的吸收极限为1.9%左右;
It was found that under different amounts of mischmetal addition, their contents did not exceed 1.6% for pure magnesium and 1.9% for AZ91D alloy in the experiments.
分析认为混合稀土的加入减少了合金液的氧化,反应形成了含稀土氯化物和氧化物的夹杂与镁合金液具有较大的密度差,有利于夹杂的沉降去除。
The mixture rare earths additions decrease the AZ91D melt oxidation and that the heavier inclusions including RECl_x and RE_xO_y are easier to sink.
分析认为混合稀土的加入减少了合金液的氧化,反应形成了含稀土氯化物和氧化物的夹杂与镁合金液具有较大的密度差,有利于夹杂的沉降去除。
The mixture rare earths additions decrease the AZ91D melt oxidation and that the heavier inclusions including RECl_x and RE_xO_y are easier to sink.