因此有必要研究材料的抗热震性。
So in the present study, the thermal shock resistance of the electrolyte was also investigated.
配制系列硅酸铝质喷补料并检测其抗热震性及喷补附着性能等。
A series of Aluminium silicate gunning refractories and its properties, such as thermal shock resistance, adhesion strength, were measured.
同时由于熔融石英本身的低热膨胀性，使其具有优良的抗热震性。
Because of the low expansion of fused quartz itself, the product possesses good thermal shock resistance.
所得带材是一种具有高比表面，高抗热震性和耐机械振动的高性能吸气材料。
Thus obtained was a high performance getter strip with high specific surface area, high resistance of thermal shock and good endurance of mechanical vibration.
尖晶石砖虽具有优良的抗热震性，但存在着热导率高及挂窑皮能力不足的缺点。
Spinel brick has the good thermal-shock resistance, however it have the disadvantages of the bad coating adherence and high heat-conducting rate.
高性能钢包浇注料，具有强度高、抗热震性好、耐侵蚀和体积稳定性好等特点。
Series high-performance ladle pouring materials are characterized by high intensity, good resistance to heat shock and corrosion and volume stability.
低导热系数，低热量的能力，良好的热稳定性和抗热震性，高强度和良好的韧性。
Low thermal conductivity, low heat capacity, excellent thermal stability and thermal shock resistance, high strength and good toughness.
实验结果表明，梯度热障涂层能明显延缓热震裂纹的形成和扩展，具有较高的抗热震性。
The test results show that retardation of thermal shock crack initiation and propagation and higher thermal shock resistance property were displayed in graded thermal barrier coating.
基质中同时引入7%的堇青石、7%的焦宝石和2%的石英砂时，浇注料的抗热震性最好。
Adding 7% cordierite, 7% flint clay and 2% quartz sand in matrix enabled the castable to have highest thermal shock resistance.
本发明属于公开了多孔碳化硅陶瓷制备技术领域的一种高抗热震性多孔碳化硅陶瓷的制备方法。
The invention discloses a preparation method of porous silicon carbide ceramics with high thermal shock resistance, belonging to the technical field of preparation of porous silicon carbide ceramics.
结果表明，白云石材料具有较高的耐高碱度渣侵蚀性、较高的抗热震性和较高的抗机械冲刷能力；
The results show that dolomite material has higher erosion-resisting characteristics to high pH value slag, higher resistant characteristics to temperature shock and higher mechanical washing.
讨论了提高陶瓷刀具材料抗热震性的方法即采用梯度功能陶瓷刀具材料，并结合断续车削试验进行了验证。
The method of improving the thermal shock resistance of ceramic tool materials i. e. using functionally gradient ceramic tool materials, is discussed and verified by intermittent turning tests.
对不同结构的膜式壁炉衬进行了抗热震性试验，并进行了传热分析，提出了膜式壁炉衬结构的优化设计方。
Thermal shock resistance tests have been conducted for various structural types of membrane wall linings along with a heat transfer analysis of the linings.
以耐火粘土、高矾土及滑石为原料研制了堇青石基陶瓷材料，并对其组织和性能尤其是抗热震性进行了研究。
Cordierite ceramics is manufactured by using the fire clay, bauxite and talc as raw materials. It's microstructure and properties, in especial the resistance to thermal shock are studied.
具有良好的抗热震性及耐磨性，温度频繁变化的高温窑炉的内衬材料，各种高温窑烧嘴浇注料或预制烧嘴砖。
Excellent thermal shock resistance and abrasion resistance, using for working lining of various high temperature kilns, various burner casting or pre-casting for high temperature kilns.
它不但具有非常好的机械加工性能、高导电性和低热膨胀系数，还具有优异的力学性能、抗氧化性能和抗热震性。
In addition to good workability, high conductivity and low thermal expansion coefficient, it has excellent mechanical properties, excellent oxidation resistance and excellent thermal shock resistance.
采用多层过渡复合涂层可有效地缓和涂层内热应力，阻碍涂层内裂纹的形成及扩展，从而大幅度提高涂层的抗热震性。
The process of destruction included three steps, they were the crack's forming, expanding and spalling. The multi layer compound coatings remarkably raised the thermal shock resist…
通过对锻造加热炉炉门破损原因的分析，制定了延长炉门使用寿命的技术措施，研制了密度低、抗热震性高的耐火浇注料。
Based on the damaging analysis of forge heating furnace gate, the technology measures are made to prolong the service life of the furnace gate.
石墨材料作为早期蒸镀金属的蒸发源材料，具有许多优良的性质，如良好的耐高温性、热稳定性，良好的导电性，较好的抗热震性能等。
Graphite which was used as evaporation source in early metal evaporation industry has excellent properties, such as excellent thermal conductivity, low resistivity, good resistance to thermal shock.
用钢纤维增强浇注料，可使工业炉窑内衬的韧性得到显著的提高，抗热震和抗冲击性得到明显改善，从而延长了它们的寿命。
Castable refractories reinforced with steel fibers can make the toughness of furnace lining and its thermal shock-resistant property raised and improved obviously, and its service life prolonged.
用钢纤维增强浇注料，可使工业炉窑内衬的韧性得到显著的提高，抗热震和抗冲击性得到明显改善，从而延长了它们的寿命。
Castable refractories reinforced with steel fibers can make the toughness of furnace lining and its thermal shock-resistant property raised and improved obviously, and its service life prolonged.