具有很好的耐磨性、弹性、扯断强度及伸长率。
Has good abrasion resistance, elasticity, tensile strength and elongation.
结果表明:炭纤维的加入能提高橡胶的硬度、耐热性及耐油性,但橡胶的扯断强度有所下降。
The results show that the presence of carbon fiber obviously enhances the hardness, heat resistance and oil resistance of the composite, but decreases the tear strength of the composite.
随着共混物中弹性体质量分数的增加,共混物的拉伸强度和弹性模量降低,扯断伸长率增大。
With the increase of elastomer content, the tensile strength and elastic modulus of the blends decreased, while the elongation at break increased.
试验结果表明,加入湿法白炭黑超细粉的试样拉伸强度比添加气相法白炭黑者提高了54%,扯断伸长率提高了64%,磨耗量降低了20%。
The results showed that the sample by adding the ultrafine powders of silica aerogel increased the tensile strength 54%, the elongation at break 64%, decreased the abrasion loss 20%.
研究聚氯乙烯/氯化聚乙烯封套材料的性能,测试封套材料的透湿率、拉伸强度和扯断伸长率。
The properties of the PVC envelop material modified by CPE was investigated, and the moisture permeability, tensile strength and elongation at break were also tested.
硬度增大,而拉伸强度和扯断伸长率则逐渐降低,随老化时间延长,变化趋势逐渐平缓。
The hardness gradually increased, while the tensile strength and elongation at break decreased gradually. With the elongation of time, these change gradually flattened.
实验结果表明,振动力场的作用可以提高TPE的拉伸强度、100%定伸应力和扯断伸长,改善TPE的硬度。
The experimental results show that, under vibration force field, tensile strength, tensile stress at 100% and elongation at break of TPE can be enhanced, and hardness(shore A) of TPE can be improved.
实验结果表明,振动力场的作用可以提高TPE的拉伸强度、100%定伸应力和扯断伸长,改善TPE的硬度。
The experimental results show that, under vibration force field, tensile strength, tensile stress at 100% and elongation at break of TPE can be enhanced, and hardness(shore A) of TPE can be improved.