介绍复合包敷层厚壁固体药柱的X射线检验透照工艺的设计和检测结果的评价。
The evaluation on the X - ray inspection technology and test results for the composite coaling thick - wall solid charge is described in the paper.
对在役废热锅炉管板角焊缝的射线检验技术进行了详细介绍,并对检验可靠性进行了讨论。
The fillet ray insqection technique for plate and tube of active service waste boiler has been introduced in details, as well as its reliability.
介绍了一种应用于钢管焊接接头检验的射线透视系统的设计原理与实现方法。
The design principle and realization method of a new kind of radiographic welding seam inspection system for steel tube were introduced.
采用宏微观检验、显微硬度测定、X射线衍射等方法对汽车发动机连杆轴瓦的失效进行了分析。
Macro examination, metallographic microscope, microhardness tester and X ray diffractometer were utilized to study the failure reasons for connecting rode bearing bush of automobile engine.
采用纵剪带钢生产小口径螺旋焊管时,超声波检验经常在焊缝的一侧发现缺陷波,而X射线拍片检验却很难发现。
The defects will be found in the seam side with ultrasonic inspection but hardly found with X ray inspection as the small diameter spiral pipe production with the split strip steel.
通过外观检验、壁厚测量、扫描电镜、能谱和X射线衍射,对省煤器管腐蚀原因进行了分析。
Through appearance inspection, wall thickness measurement, EDS analysis and X-ray diffraction, the corrosion cause of the coal economizer tube is analysed.
检查病人并根据病人的病史进行实验室检验,X射线和其他诊断治疗,同其他医生商议评估病人的身体和精神健康状况。
Examine patients and take their histories, order laboratory tests, X-rays and other diagnostic procedures and consult with other medical practitioners to evaluate patients' physical and mental health.
X射线防护材料屏蔽性能及检验方法。
Shielding performance and test methods of protection material against X-rays.
上海石化总厂热电厂除氧器水箱,经着色探伤、x射线探伤、金相检验等方法检测后,发现焊缝有大量裂纹。
Through dye check, X-ray test, and metallographic examination, quite a lot of cracks were found in the welds of a deaerator storage tank at the cogeneration plant of Shanghai Petrochemical Works.
采用宏观检查、扫描电镜、X射线能谱、金相检验、化学成分分析等方法,对金属波纹软管开裂的原因进行分析。
The methods of visual inspection, SEM, X-ray EDS, metallography and chemical composition analysis were adopted to research the rupture of flexible metal hose.
利用金相显微镜、X射线衍射仪及电子探针等对Q 345热轧钢板因冷弯产生的裂纹进行了系统检验分析。
The present paper systematically checks and examines as well as analyzes causes to the cold-bended crack in the hot rolled steel plate Q345 by microscope, X-ray and Electron Probe Micro-analyzer.
使用扫描电镜(SEM)、X射线衍射(XRD)、X射线能量色散谱仪(EDAX)、显微硬度仪等设备检验了涂层的组织和性能。
The microstructure and mechanic performances of the coating were tested by SEM, XRD, EDAX, microhardness tester and other equipments.
通过宏观和微观分析、理化性能检验、X射线衍射和模拟试验,对腐蚀油管进行了失效分析。
The failure cause of the tubing was studied by macro and micro analysis, physical and chemical properties testing, X-ray energy spectrum analysis and stimulated corrosion test.
介绍了在外壳检验中,应用X射线荧光光谱法(XRF),对外壳的镀涂层厚度进行测试;
Measurement of coating thickness in the proof-test of IC packages and metal cases using X-Ray Fluorescence (XRF) spectrometry is described.
结果表明:射线探伤检验,中压电子束焊接合格率优于高压电子束焊接;
The results show that the qualified ratio of medium-pressure electron beam welding is higher than high-pressure electron beam welding in radiographic inspection.
结果表明:射线探伤检验,中压电子束焊接合格率优于高压电子束焊接;
The results show that the qualified ratio of medium-pressure electron beam welding is higher than high-pressure electron beam welding in radiographic inspection.