XRD分析表明多孔氧化铝膜为非晶态结构。
本文介绍了近年来有关多孔氧化铝膜在功能化应用方面的进展。
In this paper, we introduce the improvement about porous anodic alumina template in applications of functional material rec...
利用阳极氧化法在酸性溶液中制备了孔洞高度有序的多孔氧化铝模板。
The main results and conclusions can be summarized as follows:AAO template with highly ordered pores was fabricated in acidic solution by using anodization method.
随着氧化时间的延长,多孔氧化铝薄膜的孔径逐渐减小,膜厚逐渐增加,但是增加的速度越来越慢。
When the anodization time extended, the pore diameters decreased, while the film thickness increased, but the increase tendency was more and more slower.
实验结果表明用表面引发原子转移自由基聚合在多孔氧化铝膜内部形成分子印迹聚合物纳米管是可行的。
The experimental results prove that atom transfer radical polymerization route works well in the formation of molecularly imprinted polymer nanotubes within porous alumina template.
本课题利用化学气相沉积(CVD)和热蒸发法在硅片称底和多孔氧化铝(aao)模板上制备纳米硅线。
Silicon nano-wires (SiNWs) were fabricated on Anodized Aluminum Oxide (AAO) template and silicon chips by the Chemical vapor Deposition (CVD) and thermal evaporation method.
采用X射线衍射、扫描电镜(sem)和光谱分析等测试技术,研究了多孔氧化铝介质膜的组成、结构以及光功能特性。
The structure and the optical functions of porous anodic films were studied by XRD, SEM and spectro-photometrical means.
在酸性电解液中,用二次阳极氧化法制备得到了高度有序的多孔阳极氧化铝模板。
Highly ordered porous anodic alumina template was prepared by twice anodic oxidation in acidulous electrolyte, and its morphology was observed by metallographic microscopy.
经溶胶-凝胶法制备的氧化铝气凝胶是一种新型耐高温的纳米多孔材料,在高温催化和高温隔热等领域具有广阔的应用前景,因而备受关注。
Synthesis of alumina aerogel via sol-gel has motivated a worldwide interest due to their application potentials in the high-temperature catalysts and high-temperature thermal insulation etc.
酸性电解液中采用电化学方法可在铝表面形成多孔阳极氧化铝膜。
Porous aluminium anodizing film can be formed on aluminium surface in acidic electrolyte solution by electrochemical method.
多孔阳极氧化铝具有耐高温、成本低、空洞分布均匀有序且大小可控等优点,是制备高度有序纳米材料的理想模板。
Porous anodic alumina membrane is an ideal template for highly ordered nanomaterials because of its low cost, high temperature resistance, uniform pore arrays and controllable pores size.
结果表明,氢氧化铝所形成的包覆层是疏松和多孔的。
The (results) reveal that the coating layer of aluminum hydroxide is loose and porous.
研究了利用氧化铝生产排放的工业废渣拜耳法赤泥为主要原料制备水处理多孔陶粒滤料的方法。
The preparation of porous ceramics with Red Mud derived from Bayer process as the main raw material for treatment of waste water in production of alumina was studied.
当氧化铝多孔膜的纳米孔排列成规则的阵列结构时,氧化铝多孔膜将具有许多其它纳米材料无法比拟的优势。
When ordered nano-pore array structure was formed on the anodized alumina, the porous alumina film will possess much more superiority than nano material prepared by others ways.
阳极氧化铝膜具有独特的多孔结构,可作为制备各种纳米功能材料的模板,因而在纳米功能材料制备中占有重要地位。
Therefore, it is very important to investigate anodic aluminum oxide films. In this paper the structure and preparation methods of porous aluminum oxide templates as well as the synthesis an...
介绍了多孔阳极氧化铝模板的制备和以多孔阳极氧化铝为模板采用常规方法制备高度有序纳米点阵列材料的最新研究进展,以及纳米点阵列的应用前景。
The article reviews the methods of template synthesis of ordered metal nanohole arrays by replication of mother templates, the characteristics and the applications of the metal template.
用阳极氧化的方法制备了阳极氧化铝膜,向其孔中镀入了铜,制备了镶嵌铜多孔铝膜。
The porous aluminium coating inlaid with copper was obtained by implanting Cu into the pores of anodic oxidation aluminium coating prepared by electroplating.
用阳极氧化的方法制备了阳极氧化铝膜,向其孔中镀入了铜,制备了镶嵌铜多孔铝膜。
The porous aluminium coating inlaid with copper was obtained by implanting Cu into the pores of anodic oxidation aluminium coating prepared by electroplating.