此结果对于选择磁带涂布的固化条件有一定意义。
These results can be used as reference data for the selection of curing conditions in the coating technology of magnetic tapes.
在固化过程发生相分离,两相的玻璃化转变温度主要取决于固化条件。
Phase separation occurs during cure processes. The glass transition temperatures depend mainly upon the cure conditions.
讨论了不同多元醇、不同氨基树脂和固化条件等因素对漆膜性能的影响。
Effects of each component and curing condition on paint properties were discussed.
介绍了各种粉末涂料的使用特点、涂装工艺、固化条件、涂层性能及影响因素。
The application characteristics, finishing technology, curing schedule, film properties, and the affecting factors were discussed.
本文讨论了消光剂、配方组成、施工和固化条件等对100%UV固化涂料光泽的影响。
The influence of matting agents, formulation, and application and curing schedule on gloss of 100% UV curing coatings is discussed.
结果表明,在相同固化条件下,纳米微波吸收剂能明显降低改性环氧胶粘剂的微波固化时间。
The results show that nanometer microwave-absorber can obviously decrease the microwave curing time of modified epoxy adhesive under the same curing condition.
本发明还提供可使铝螯合物系潜固化剂的固化条件比较容易控制的铝螯合物系潜固化剂的制备方法。
Also disclosed is a process for producing the aluminum chelate type latent curing agent, which can control the curing conditions for the latent curing agent relatively readily.
这些涂料树脂的基本新颖性在于,它们不需要添加传统的光引发剂在标准UV固化条件下即可固化。
An essential novelty of these coating resins is that they will cure under standard UV-cure conditions without the addition of traditional photoinitiators.
对白炭黑对胶粘剂的热稳定性的影响进行了测试,研究了白炭黑的加入量和胶粘剂的固化条件对耐焊时间的影响。
Through testing the thermal stability of silica and adhesives, we study how the amount of silica and the cure of adhesives affect the soldering time.
提出了该涂料的固化可通过优化催化剂用量和固化条件来控制,流挂可通过添加流动控制剂来控制,并列举了它们的试验结果。
The curing process can be controled through optimum catalyst amount and curing conditions, sagging can be controled by rheology control agent. The test results were listed.
本文研究了单组分湿固化聚氨酯胶粘剂合成中的规律,如NCO/OH比例对反应及产品性能的影晌以及固化条件对粘接性能的影响。
This paper explored the rules of the synthesis, such as the effect of the NCO/OH and the curing condition on the performance and reaction.
水热热压固化温度是影响固化体性能的重要条件,可以利用固化体组分的改变及固化条件的控制来调节固化体表面酸性及其催化性能。
The surface acidity and catalytic characters of solidified bodies can be adjusted by means of changing compositions of the initial mixture and the conditions of solidification.
对磷酸氧化铜无机胶套接扭剪试件在不同粘接表面状态,不同固化条件下的扭剪强度进行了系统测试,得出了对实际应用有价值的结论。
Under various adherent condition and solidify condition, the Torsional shear strength of the copper phosphate inorganic adhesive were tested. The results which are useful to application were obtained.
通过进一步对胶粘剂的固化条件、耐介质性能及耐湿热老化性能的考查,说明J-200-1D胶粘剂具有优异的工艺性能及耐候性能。
The tests of curing condition, resistance to medium and hydrothermal ageing showed that the J-200-1D adhesive has excellent processing properties and resistance to weathering.
采用我国海南岛产腰果油制得的槚如果酚合成了高邻位热固性酚醛树脂,并对所合成的树脂的结均、固化条件、固化后树脂的性能进行了分析。
The paper analyses the structure, curing conditions and the properties of the cardanol resol which can be made from cashew nut oil produced in Hainan Island.
本文着重从银粉的粒度、添加量和固化剂的种类、用量以及固化条件等方面研究和探讨了环氧-低分子聚酰胺-银粉导电胶体系的导电性及强度。
In this paper the effect of size of silver particles, proportion, curing agent and curing condition on epoxy resin - low - molecular polyamide - silver particles system are studied and discussed.
结果表明,在粘接过程中采用适当的表面处理方法、涂胶方式,确定适当的加压压力、涂胶厚度和固化条件,有利于减小粘接件拉伸强度数据的分散性并提高粘接强度。
The results showed that choosing of proper manners of surface treatment and adhesive coating as well as setting of pressure, thickness of adhesive and curing condition were helpful to improve t...
任何液体在一定条件下均可固化。
Any liquid could be solidified under the certain conditions.
按电玉粉重量计,在搅和机中加入0.3~0.4%,所有原来其他的固化剂都不必加入,原来的生产工艺条件不变。
SH-1 in term of weight of moulding powders, and no other curing agent is needed. Follow the processing steps of moulding powders mixing with former curing agent.
文中应用总放热系数等效考虑了CFRP压力容器固化过程中热压釜辐射与对流边界条件。
General heat release coefficient is used to equivalently consider autoclave radiation and convection of boundary condition during curing process for CFRP pressure vessel.
文章第二部分讨论了集装箱无气喷涂工艺条件、操作要点和自动喷漆工艺特点,以及集装箱涂膜的干燥与固化。
In the second part, process condition, operational gist and process characteristic of container airless spraying, container films drying and curing were discussed.
对纳米yTZP(氧化钇稳定)坯片在新型水基凝胶流延成型工艺中,气氛条件对浆料固化过程的影响进行了研究。
The influence of atmosphere condition on solidification procedure of nanometer tetragonal polycrystals zirconia (YTZP) slurry in the AqueousGelTapeCasting process was investigated.
液体侵渍模塑使用低粘度的硅树脂,在低压和低温条件下抽运,在极短的时间内固化,与固体材料相比,废弃物少。
Liquid injection molding utilizes low viscosity silicones which can be pumped at lower pressure and temperature, and cure in significantly less time and with less waste than solid materials.
厌氧密封粘合剂是在缺氧条件下固化而起密封粘合作用的一种精细化学品。
Anaerobic sealants and adhesives are fine chemicals, which are used in sealing and bonding after curing in the absence of oxygen.
采用此方法增韧的环氧树脂,贮存稳定性好,在加热及室温条件下固化,均能获得较高的剪切强度和T -剥离强度。
The epoxy resin toughened by the above copolymer has excellent storage stability and, after cured by heating or at room temperature, it has higher shear strength and T-peeling strength.
评价光固化窝沟封闭在一般条件下用于预防龋病的效果。
To observe the clinical effect on the prevention of caries of pit and fissure sealant of light solidify.
在实验室与生产现场两种条件下将光纤折射率传感器埋设于预浸料中对其固化工艺过程进行了监测。
Tests were also carried out in composite manufacture, in which the fiber optic refractive sensors were embedded in the prepreg during the cure process.
研究了热固性不饱和聚酯常温固化制造新型塑料电热板的配方、成型工艺路线与成型条件。
A new pattern plastic galvanothermy board can be made by solidifying heat set unsaturated polyester resin at normal temperature.
在较高温度和较低纤维含量条件下,离子导电率变化较快,对树脂固化反应的影响较大;
In the case of high temperature and low fabric volume fraction, the ionic conductivity changes dramatically, which in turn has a significant influence on the resin curing process.
在较高温度和较低纤维含量条件下,离子导电率变化较快,对树脂固化反应的影响较大;
In the case of high temperature and low fabric volume fraction, the ionic conductivity changes dramatically, which in turn has a significant influence on the resin curing process.